The effect of phase angle on crack growth mechanisms under thermo-mechanical fatigue loading
نویسندگان
چکیده
منابع مشابه
Thermo-Mechanical Fatigue Crack Growth of RR1000
Non-isothermal conditions during flight cycles have long led to the requirement for thermo-mechanical fatigue (TMF) evaluation of aerospace materials. However, the increased temperatures within the gas turbine engine have meant that the requirements for TMF testing now extend to disc alloys along with blade materials. As such, fatigue crack growth rates are required to be evaluated under non-is...
متن کاملHold-time effect on the thermo-mechanical fatigue crack growth behaviour of Inconel 718
In-phase TMF crack growth testing with different lengths of the hold time at the maximum temperature of 550C has been conducted on Inconel 718 specimens. Focus has been on establishing a method for TMF crack growth testing and investigating the effect of high temperature hold times on the TMF crack growth of the material. The tests are compared to isothermal crack propagation tests and show go...
متن کاملEffect of Boundary Condition on Pre-Existing Crack Under Fatigue Loading
In this paper, the present investigation has been conducted keeping in mind some of the problems concerning the crack propagation direction and growth under constant loading in an inclined crack geometry. The present studies mainly focused on the development and modifications in the crack growth criterion to account the biaxial, shear loading and number of stress terms. Existing criteria for th...
متن کاملThe Effect of Various Parameters on Out-of-phase Thermo-mechanical Fatigue Lifetime of A356.0 Cast Aluminum Alloy
In this paper, the effect of various parameters on out-of-phase thermo-mechanical fatigue (OP-TMF) lifetime of A356.0 cast aluminum alloy is investigated. The studied parameters include maximum temperature, dwell time, and the thermo-mechanical loading factor. OP-TMF tests are conducted considering realistic running conditions of diesel engine cylinder heads. The maximum temperature varies betw...
متن کاملAnalyses of Fatigue and Fatigue-crack Growth under Constant- and Variable-amplitude Loading
Studies on the growth of small cracks have led to the observation that fatigue life of many engineering materials is primarily “crack growth” from micro-structural features, such as inclusion particles, voids, slip-bands or from manufacturing defects. This paper reviews the capabilities of a plasticity-induced crack-closure model to predict fatigue lives of metallic materials using “small-crack...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: International Journal of Fatigue
سال: 2020
ISSN: 0142-1123
DOI: 10.1016/j.ijfatigue.2020.105539