Evaluation of Micron-Sized Wood and Bark Particles as Filler in Thermoplastic Composites
Micron-sized particles, prepared from loblolly pine (Pinus taeda L.) wood and bark, were evaluated for use in wood-plastic composites (WPCs). Particles were also prepared from hard (periderm) and soft (obliterated phloem) components in the bark and compared to whole wood (without bark) filler commonly used by the WPC industry. All bark fillers had different thermal degradation profiles and high...
متن کاملDurability of wood plastic composites manufactured from recycled plastic
The influence of accelerated weathering, xenon-arc light and freeze-thaw cycling on wood plastic composites extruded from a recycled plastic was studied. The results showed that, in general, weathering had a stronger impact on samples made from plastic waste compared to a sample made from virgin material. After weathering, the mechanical properties, tensile and flexural, were reduced by 2-30%, ...
متن کاملSome of the Properties of Wood Plastic Composites
In this study some of the important properties of experimentally manufactured wood– plastic composites (WPC) were determined. Specimen having 60% and 80% particle and fibre of radiata pine (Pinus radiata ) were mixed with polypropylene (plastic) and four different additives, namely Struktol TR 016 which is coupling agent, CIBA antimicrobial agent (IRGAGUARD F3510) as fungicide, CIBA UV filter c...
متن کاملWeathering Characteristics of Wood Plastic Composites Reinforced with Extracted or Delignified Wood Flour
This study investigated weathering performance of an HDPE wood plastic composite reinforced with extracted or delignified wood flour (WF). The wood flour was pre-extracted with three different solvents, toluene/ethanol (TE), acetone/water (AW), and hot water (HW), or sodium chlorite/acetic acid. The spectral properties of the composites before and after artificial weathering under accelerated c...
متن کاملProperties of Flat-Pressed Wood Plastic Composites Containing Fire Retardants
This study investigated physical, mechanical, and fire properties of the flat-pressed wood plastic composites (WPCs) incorporated with various fire retardants (FRs) [5 or 15% by weight (wt)] at 50 wt % of the wood flour (WF). The WPC panels were made from dryblended WF, polypropylene (PP) with maleic anhydridegrafted PP (2 wt %), and FR powder formulations using a conventional flat-pressing pro...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Maderas. Ciencia y tecnología
سال: 2013
ISSN: 0718-221X
DOI: 10.4067/s0718-221x2013005000028