The Effect of Aluminium Injection Parameters on the Mechanical Properties of the Material Produced by High Pressure Die-Casting

Aluminium is one of the basic materials used in many sectors, especially automotive, defence and aviation. Generally, aluminium parts are manufactured by using injection molding methods such as etc. Injection presses that for die-casting material have a lot parameters, affect molded parts’ properties. In this study, effect parameters on mechanical properties was investigated. Firstly, test part shaped currently press machine sector found out. An aluminum alloy, named Al〖Si〗_12 Cu (EN AC 47000), widely techniques preferred. Three as, velocity (m/s), time mold opening (s) molten metal temperature (0C), were selected. And all works planned with full factorial experimental design method. Thus, an machine. Moreover, tests, hardness tensile, performed to investigate material. The tests analysed ANOVA As results analysis, highest value obtained 85 HB when 750 ℃, 1.3 m/s, 10 s, breaking strength 725 4 12 s be 264 MPa.