The Crystal Chemistry of Nepheline
The crystal structures of three nepheline samples, (1) K1.91 Na6.04 Si8.15 Al7.72 Fe0.10 O32, a 9.9995(6), c 8.384(2) Å, P63, Z = 1, Dx = 2.673 g cm–3, from the Khibina–Lovozero complex, Kola Peninsula, Russia, (2) K1.60 Na6.21 Ca0.08 Si8.44 Al7.43 O32, a 9.985(1), c 8.372(1) Å, P63, Z = 1, Dx 2.660 g/cm3, from Bancroft, Ontario, Canada, and (3) K1.76 Na5.86 Ca0.13 Si8.12 Al7.84 Fe0.04 O32, a 9...
متن کاملModulated structure of nepheline.
The incommensurately modulated structure of a natural nepheline of composition K(0.54)Na(3.24)Ca(0.03)Al(3.84)Si(4.16)O(16) has been determined in superspace. The compound crystallizes in the trigonal centered superspace group X3(00γ)0 with γ = 0.2048 (10), X = (0, 0, 0, 0), (1/3, 2/3, 0, 2/3), (2/3, 1/3, 0, 1/3), a = 17.2889 (8) and c = 8.3622 (10) Å. The structure is characterized by a framew...
متن کامل[Crystal chemistry of hydroxyapatite].
X線 回折 法 に よる結 晶構 造 解 析 は,大 き さ0 .1 ~1mmの 単 結 晶 が あ れ ば ,原 子 の三 次 元 配 列 を 決 定 す る こ とが で き,原 子 間 距 離,結 合 角,配 位 数 な どの化 学 結 合 に 関 す る知 識 が 直 接 得 られ る非 常 に 優 れ た 方法 で あ る。 結 晶構 造 を決 定 す る過 程 は,次 の二 つ の段 階 に分 け られ る。 第1は ,単 結 晶 を 選 んで ワイ セ ンベ ル グ写 真 法 な どに よ って 晶 系,格 子 定 数,空 間 群 を 決 め,比 重 測 定 に よ って 単 位 格 子 内 の 化 学 単 位 数 を 決 定 す る過程 で あ る。 第2は,単 結 晶 のX線 回 折 強 度 か ら各原 子 の座 標 を 決 定 す る過 程 で あ る。 こ の過...
متن کاملCrystal Chemistry of Boehmite
-Thirty two boehmites, synthesized at temperatures ranging from room temperature to 300~ were examined by scanning electron microscopy, transmission electron microscopy, electron diffraction, X-ray powder diffraction, differential thermal analysis, and infrared spectroscopy. The results show that boehmite exhibits a continuous gradation in crystallite size ranging from single octahedral layers ...
متن کاملSingle-crystal Xrd, Tem, and Thermal Studies of the Satellite Reflections in Nepheline
A sample of nepheline from Egan Chute, near Bancroft, Ontario, with a chemical composition (K1.32 0.68)(Na6.05Ca0.22) [Al7.77Si8.21O32], has been studied using single-crystal X-ray diffraction, transmission electron microscopy (TEM), thermal analyses, and powder X-ray diffraction. Its structure was refined in space group P63 to an R1 index of 0.041 on the basis of 737 unique observed reflection...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: The Canadian Mineralogist
سال: 2003
ISSN: 0008-4476,1499-1261
DOI: 10.2113/gscanmin.41.1.61