The Aging Characteristics of Mg-6 wt.% Al-1 wt.% Zn Alloy Prepared by Gas Atomization
نویسندگان
چکیده
منابع مشابه
تولید و مشخصه یابی کامپوزیت نانوساختار Al-Mg-Zn/ 3 wt.% Al2O3 بوسیله زمینه پیش آسیاب شده توسط آلیاژسازی مکانیکی
Al-Zn-Mg/3 wt-% Al2O3 nanostructured composite powder was synthesized through Mechanical Alloying (MA). At first, the 7014 alloy matrix constituents were milled in a planetary ball mill for 20 hours. Then, 3 wt.% µ-Al2O3 particles were added to the pre-milled matrix and the nanostructured composite powder was produced at different MA times to investigate the effects of MA time ...
متن کاملNanocrystalline Al7075 + 1 wt % Zr Alloy Prepared Using Mechanical Milling and Spark Plasma Sintering
The microstructure, phase composition, and microhardness of both gas-atomized and mechanically milled powders of the Al7075 + 1 wt % Zr alloy were investigated. The gas-atomized powder exhibited a cellular microstructure (grain size of a few µm) with layers of intermetallic phases along the cell boundaries. Mechanical milling (400 revolutions per minute (RPM)/8 h) resulted in a grain size reduc...
متن کاملEFFECT OF COOLING RATE AND GRAIN REFINEMENT ON THE MICROSEGREGATION IN Al-4.8 wt.% Cu ALLOY
Microsegregation is one of the most important phenomena occurs during solidification. It usually results in formation of some unexpected second phases which generally affect the mechanical properties and specially reduce the workability of casting products. The aim of this research is to study the effect of cooling rate and grain refinement on the microsegregation in Al-4.8 wt.% Cu. For this p...
متن کاملCo-Precipitation, Strength and Electrical Resistivity of Cu–26 wt % Ag–0.1 wt % Fe Alloy
Both a Cu-26 wt % Ag (Fe-free) alloy and Cu-26 wt % Ag-0.1 wt % Fe (Fe-doping) alloy were subjected to different heat treatments. We studied the precipitation kinetics of Ag and Cu, microstructure evolution, magnetization, hardness, strength, and electrical resistivity of the two alloys. Fe addition was incapable of changing the precipitation kinetics of Ag and Cu; however, it decreased the siz...
متن کاملThe microstructure , tensile properties , and creep behavior of Mg – Zn alloys containing 0 – 4 . 4 wt . % Zn
This paper describes the microstructure, tensile, and tensile–creep behavior of a series of Mg–Zn alloys ranging from 0 to 4.4 wt.% Zn. The microstructures consisted of equiaxed hexagonal-close-packed grains with fine precipitates preferentially located at grain boundaries. Some of the microstructures contained fine laths within the equiaxed grains. The finest grain sizes were observed for a Zn...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Korean Powder Metallurgy Institute
سال: 2009
ISSN: 1225-7591
DOI: 10.4150/kpmi.2009.16.4.275