The Age Hardening Mechanism of Nanocrystalline Ni-P Alloys Synthesized by Electrodeposition
نویسندگان
چکیده
منابع مشابه
HIGH-STRENGTH NANOCRYSTALLINE Ni-W ALLOYS PRODUCED BY ELECTRODEPOSITION
Nanocrystalline Ni-W alloys having both high ductility and high strength were produced by electrodeoisition. The plating bath for the electrodeposition contained nickel sulfate, citric acid, sodium tungstate and ammonium chloride, and was operated at various bath concentrations and conditions of electrolysis. The ductility and tensile strength of the deposited alloys are strongly influenced by ...
متن کاملTernary Ni-Fe-Co Alloys Nanowire Electrodeposition
Nanowire is a cylindrical nano-structure with nanometer dimensions. In this research, the studied nanowire was made from the magnetic triple Ni-Fe-Co alloy. We utilized ordered porous anodic aluminum oxide as a template for the nanowire deposition. The nanowire arrays were electrodeposited in the cylindrical pores of the oxide layer by AC potential in a simple sulfate bath. Then the relation ...
متن کاملTernary Ni-Fe-Co Alloys Nanowire Electrodeposition
Nanowire is a cylindrical nano-structure with nanometer dimensions. In this research, the studied nanowire was made from the magnetic triple Ni-Fe-Co alloy.
 We utilized ordered porous anodic aluminum oxide as a template for the nanowire deposition. The nanowire arrays were electrodeposited in the cylindrical pores of the oxide layer by AC potential in a simple sulfate bath. Then the relatio...
متن کاملHot Nanoindentation of Nanocrystalline Ni-W Alloys
High temperature nanoindentation experiments are conducted to assess the activation enthalpy for deformation of nanocrystalline Ni-W alloys, for grain sizes between 3 and 80 nm. Thermal softening becomes less pronounced at finer grain sizes, and the activation enthalpy has an apparent inflection at a grain size near ~10-20 nm, in the vicinity the Hall-Petch breakdown. This inflection is related...
متن کاملMechanically driven grain boundary relaxation: a mechanism for cyclic hardening in nanocrystalline Ni
Molecular dynamics simulations are used to show that cyclic mechanical loading can relax the non-equilibrium grain boundary (GB) structures of nanocrystalline metals by dissipating energy and reducing the average atomic energy of the system, leading to higher strengths. The GB processes that dominate deformation in these materials allow low-energy boundary configurations to be found through kin...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Society of Materials Science, Japan
سال: 2013
ISSN: 0514-5163,1880-7488
DOI: 10.2472/jsms.62.710