Tension-compression fatigue of WC-12%Co hardmetal.
نویسندگان
چکیده
منابع مشابه
Cumulative Fatigue Damage Under stepwise Tension-Compression Loading
Rock structures are subjected to cyclic tension-compression loading due to a blasting, earthquake, traffic and injection-production in underground storage case. Therefore study the fatigue behavior of rock samples under this type of loading is required. In this study, the accumulated fatigue damage for a Green Onyx rock sample which consisted of only one mineral composition with two-step high-l...
متن کاملNew results on the relationship between hardness and fracture toughness of WC-Co hardmetal
Two sets of WC-Co grades were produced, with cobalt content ranging from 3 to 50 wt.%. The mean grain size of the two sets was 2.2 and 6 ~tm respectively. The two sets of grades were used to investigate the relationship between hardness and fracture toughness. It was found that at constant WC grain size the relationship is linear. It was also found that in the low toughness range, grades of equ...
متن کاملTension–tension fatigue of hybrid composite rods
The tension–tension fatigue behavior was investigated for a hybrid composite rod comprised of a unidirectional carbon fiber core and a glass fiber shell. Fatigue tests were performed at three R-ratios and four maximum applied stress levels (MAS) while recording the secant modulus at each cycle, and acoustic emission (AE) sensors were employed to monitor the activation of fatigue mechanisms. Fat...
متن کاملFRACTURE AND FATIGUE BEHAVIOR OF WC-Co AND WC-CoNi CEMENTED CARBIDES
The fracture and fatigue characteristics of several cemented carbide grades are investigated as a function of their microstructure. In doing so, the influence of binder chemical nature and content (Co and 76wt%Co-24wt%Ni), as well as carbide grain size on hardness, flexural strength, fracture toughness and fatigue crack growth (FCG) behavior is evaluated. Mechanical testing is combined with a d...
متن کاملExperimental and Numerical Study of Residual Stress in the WC-12Co HVOF Sprayed Coatings
Thermally sprayed coatings are intrinsically associated with residual stresses in the deposits. These stresses are varied in nature and magnitude, and have a pronounced effect on the mechanical behavior of the system. In the current study, WC-12Co coatings were deposited using HVOF thermal spraying. The sin2ψ method was used to evaluate the through thickness residual stress by means ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Society of Materials Science, Japan
سال: 1987
ISSN: 1880-7488,0514-5163
DOI: 10.2472/jsms.36.135