Tensile bond strength of cold roll bonded aluminium sheets
نویسندگان
چکیده
منابع مشابه
Micro-tensile bond strength of adhesives bonded to Class-I cavity-bottom dentin after thermo-cycling.
UNLABELLED A widely used artificial aging methodology is thermo-cycling. The ISO TR 11450 standard (1994) recommends 500 cycles in water between 5 and 55 degrees C. Recent literature revealed that more cycles are needed to mimic long-term bonding effectiveness. Furthermore, the artificial aging effect induced by thermo-cycling is not clearly established. Two underlying mechanisms can be advance...
متن کاملInverse relationship between tensile bond strength and dimensions of bonded area.
It is a known fact that there is a relationship between magnitude of bonded area and laboratory tensile test results. This relationship has been described for a range of areas between 1 and 10 mm(2), in extracted, nonperfused teeth. The aim of this study is to test this relationship in perfused teeth, with bonded areas ranging from 0.7 to 110.9 mm(2). Dentin of 92 sound third human molars was e...
متن کاملAn investigation on the bond strength of aluminum strips in presence of brass mesh after cold roll bonding
In the present study, the presence of brass mesh on the bond strength of aluminum (AA1050) strips in the cold roll bonding process was investigated. The influence of various process parameters including reduction in thickness, pre-rolling annealing, initial thickness of the strips, and post-rolling annealing was also considered. After cold roll bonding process, peeling test was carried out and ...
متن کاملAnnealing Effects in Twin-Roll Cast AA8006 Aluminium Sheets Processed by Accumulative Roll-Bonding
Ultrafine grained sheets were prepared from a twin-roll cast AA8006 aluminium alloy using accumulative roll-bonding process at room temperature. The evolution of microstructure of sheets after three accumulative roll-bonding passes during isochronal annealing with a constant step of 20 °C/20 min was studied by light and electron microscopy. The influence of the resulting microstructure on mecha...
متن کاملMicrostructural Evolution of Roll Bonded Al-Clad Stainless Steel Sheets at Elevated Temperatures
The cold roll bonding of Al on AISI 304L stainless steel was carried out to fabricate the Al/304L/Al clad sheet composites. The maximum bond strength of 20 N/mm was acquired just by 38% reduction, for which the tearing of the aluminum sheet occurred during the peeling test. The microstructural evolution during subsequent postannealing heat treatment was systematically studied based on the impur...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Materials Processing Technology
سال: 2013
ISSN: 0924-0136
DOI: 10.1016/j.jmatprotec.2013.01.007