Temporal Evolution of GP Zones in an Al-Ag Alloy
نویسندگان
چکیده
منابع مشابه
Phase Transformation Induced Self-Healing Behavior of Al-Ag Alloy
Self-healing alloys are promising materials that can decrease the consequences of accidents. To detect crack formation in a material is simple task that can be performed by e.g., sonic or ultrasound detection, but it is not always possible to immediately replace the damaged parts. In this situation, it is very advantageous to have the chance to heal the crack during operation, which can be done...
متن کاملTHREE DIMENSIONAL ATOM PROBE ANALYSIS OF PRE-PRECIPITATE CLUSTERING IN AN Al-Cu-Mg-Ag ALLOY
Trace element additions in age hardening aluminum alloys often modify precipitation products and kinetics. In the case of Al-Cu alloy, combined addition of trace amount of Mg and Ag leads to precipitation of fine and uniform dispersions of plate-like Ω phase on the {111}Al planes in addition to the θ′ precipitates on the {001}Al planes [1,2]. The Ω phase shows high thermal stability and resista...
متن کاملEffect of Deformation-Induced Defects on the Microstructure and Pitting Corrosion Behavior of Al-Ag Alloy
In this study, a wide range of combined ageing treatments and cold work deformations in the Al 4.2 wt% Ag alloy matrix were proposed, aiming to investigate the effect of defects such as precipitates (Ag2Al plates) and dislocations on the mechanical and electrochemical behavior of Al–4.2 wt% Ag alloys. Further reductions of thickness from 10 to 60%, decreases the mean size of Ag2...
متن کاملEvolution of texture in an ultrafine and nano grained magnesium alloy
The evolution of texture was discussed during the formation of ultra-fine and nano grains in a magnesium alloy severely deformed through accumulative back extrusion (ABE). The microstructure and texture obtained after applying multiple deformation passes at temperatures of 100 and 250°C were characterized. The results showed that after single ABE pass at 100°C an ultrafine/nano grained microstr...
متن کاملPreprint of a manuscript submitted to Acta Materialia EVOLUTION OF W PHASE IN AN Al-Cu-Mg-Ag ALLOY Ð A THREE DIMENSIONAL ATOM PROBE STUDY
Evolution of plate-like precipitate of the W phase in an Al-1.9Cu-0.3Mg-0.2Ag (at.%) alloy has been investigated by three dimensional atom probe (3DAP) and transmission electron microscope (TEM) techniques. In an as-quenched alloy, all solute atoms are uniformly dissolved. After 5 s aging at 180¡C, coclusters of Ag and Mg atoms are present. Initially, these co-clusters do not have well defined ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Microscopy and Microanalysis
سال: 2006
ISSN: 1431-9276,1435-8115
DOI: 10.1017/s1431927606068140