Temporal Evolution of Corrosion Film Nano-Porosity and Magnesium Alloy Hydrogen Penetration in NaCl Solution
نویسندگان
چکیده
منابع مشابه
Oxide Film and Porosity Defects in Magnesium Alloy Az91
Porosity is a major concern in the production of light metal parts. This work aims to identify some of the mechanisms of microporosity formation in magnesium alloy AZ91. Microstructure analysis was performed on several samples obtained from gravity-poured ingots in graphite plate molds. Temperature data during cooling was acquired with type K thermocouples at 60 Hz at three locations of each ca...
متن کاملPrediction of corrosion rate of AZ31B magnesium alloy under salt fog environment in NaCl solution
Magnesium alloys have gained considerable interest as a material for automotive and aerospace applications due to its low density, high specific strength, and good castability. However, another considerable issue is their corrosion properties. This restricts their practical applications. In this present research, corrosion behavior of the AZ31B magnesium alloy was evaluated by conducting salt f...
متن کاملEvolution of texture in an ultrafine and nano grained magnesium alloy
The evolution of texture was discussed during the formation of ultra-fine and nano grains in a magnesium alloy severely deformed through accumulative back extrusion (ABE). The microstructure and texture obtained after applying multiple deformation passes at temperatures of 100 and 250°C were characterized. The results showed that after single ABE pass at 100°C an ultrafine/nano grained microstr...
متن کاملCorrosion behaviour of friction stir welded AZ61A magnesium alloy welds immersed in NaCl solutions
The extruded AZ61A magnesium alloy plates of 6 mm thickness were butt welded using friction stir welding (FSW) process. The corrosion behavior of the welds was evaluated by conducting immersion test in NaCl solution at different pH value, immersion time and chloride ion concentrations. An empirical relationship was established incorporating pH value, immersion time and chloride ion concentratio...
متن کاملMitigation of Corrosion on Magnesium Alloy by Predesigned Surface Corrosion
Rapid corrosion of magnesium alloys is undesirable in structural and biomedical applications and a general way to control corrosion is to form a surface barrier layer isolating the bulk materials from the external environment. Herein, based on the insights gained from the anticorrosion behavior of corrosion products, a special way to mitigate aqueous corrosion is described. The concept is based...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of The Electrochemical Society
سال: 2020
ISSN: 1945-7111
DOI: 10.1149/1945-7111/abbdd0