Critical assessment 20: On carbon excess in bainitic ferrite
For several decades, the question of carbon supersaturation in bainitic ferrite has attracted the attention of physical metallurgists. Originally, this was associated with excess carbon due to the displacive nature ofphase transformation and its subsequent trappingatdefects inbainitic ferrite. The development of advanced experimental techniques, such as atom probe tomography and in situ synchro...
متن کاملتأثیر چگالی نابجایی‌ها بر رفتار تغییر شکل فولاد بینیتی فوق مستحکم
Presence of nanoscale bainitic ferrites and high carbon retained austenites that are stable at ambient temperature within the microstructures of super strong bainitic steels makes it possible to achieve exceptional strengths and ductility properties in these groups of nanostructured steels. This article aims to study the effect of the dislocation density variations during tensile testing in amb...
متن کاملSolute Trapped at Defects during the Displacive Formation of Bainitic Ferrite
New developments with bainite have resulted in a steel with an ultimate tensile strength of 2500 MPa, a hardness of 600-670 HV and a toughness in excess of 30-40 MPa m [1]. The novel microstructure is generated in a high carbon (0.98 wt.%) high silicon (1.46 wt.%) steel austenitized for 15 min. at 1000 oC, and then isothermally transformed at temperatures of ∼200 oC. Iron does not diffuse durin...
متن کاملHigh-Strength Bainitic Steels
With careful design, mixed microstructures consisting of fine plates of upper bainitic ferrite separated by thin films of stable retained austenite have exhibited impressive combinations of strength and toughness in highsilicon bainitic steels. The silicon suppresses the precipitation of brittle cementite leading to an improvement in toughness. The essential principles governing the optimisatio...
متن کاملStrong Bainitic Steels by Continuous Cooling Transformation
Using metallurgical models, three steels were designed to obtain carbide-free bainitic structures in the as-rolled condition. Experimental castings were hot-rolled in a pilot mill and their austenite decomposition kinetics were measured using dilatometry. Tensile and Charpy impact properties were measured and the microstructures were characterised using X-ray diffractometry, optical and scannin...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Scripta Materialia
سال: 2012
ISSN: 1359-6462
DOI: 10.1016/j.scriptamat.2012.08.007