Table-like magnetocaloric effect in Gd56Ni15Al27Zr2 alloy and its field independence feature
In order to obtain “table-like” magnetocaloric effect (MCE), multiple-phase Gd56Ni15Al27Zr2 alloy was prepared by arc-melting followed by suck-casting method. Powder x-ray diffraction and calorimetric measurements reveal that the sample contains both glassy and crystalline phases. The fraction of the glassy phase is about 62%, estimated from the heat enthalpy of the crystallization. The crystal...
متن کاملExchange Bias and Inverse Magnetocaloric Effect in Co and Mn Co-Doped Ni2MnGa Shape Memory Alloy
Exchange bias effect observed in the Ni1.68Co0.32Mn1.20Ga0.80 alloy confirms the coexistence of antiferromagnetic and ferromagnetic phases in the martensite phase. A large inverse magnetocaloric effect has been observed within the martensitic transformation temperature range, which is originated from modified magnetic order through magnetic-field-induced phase transformation from partially anti...
متن کاملThe magnetocaloric effect and critical behaviour of the Mn(0.94)Ti(0.06)CoGe alloy.
Structural, magnetic and magnetocaloric properties of the Mn(0.94)Ti(0.06)CoGe alloy have been investigated using x-ray diffraction, DC magnetization and neutron diffraction measurements. Two phase transitions have been detected, at T(str) = 235 K and T(C) = 270 K. A giant magnetocaloric effect has been obtained at around T(str) associated with a structural phase transition from the low temper...
متن کاملTwo successive magneto-structural transformations and their relation to enhanced magnetocaloric effect for Ni55.8Mn18.1Ga26.1 Heusler alloy
In the present work, two successive magneto-structural transformations (MSTs) consisting of martensitic and intermartensitic transitions have been observed in polycrystalline Ni55.8Mn18.1Ga26.1 Heusler alloy. Benefiting from the additional latent heat contributed from intermediate phase, this alloy exhibits a large transition entropy change ΔStr with the value of ~27 J/kg K. Moreover, the magne...
متن کاملMagnetocaloric effect in La0.75Sr0.25MnO3 manganite
The polycrystalline manganite La0.75Sr0.25MnO3 prepared by an alternative carbonate precipitation route reveals the rhombohedral perovskite structure. Magnetization isotherms measured up to 2 T are used to determine Curie temperature of 332 K by means of Arrott plot. Maximum of magnetic entropy change is found at Curie temperature. The relative cooling power equal to 64 J/kg for 1.5 T magnetic ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Applied Physics
سال: 2015
ISSN: 0021-8979,1089-7550
DOI: 10.1063/1.4931765