Large scale synthesis of highly pure single crystalline tellurium nanowires by thermal evaporation method.
Single crystalline tellurium nanowires were successfully synthesized in large scale by a facile approach of vaporizing tellurium metal and condensing the vapor in an inert atmosphere onto a Si substrate. Tellurium was evaporated by heating at 300 degrees C at 1 torr and condensed on the Si substrate at 100-150 degrees C, in the downstream of argon (Ar) gas at a flow rate of 25 sccm for 30 min. ...
متن کاملSynthesis of Chromium Oxide Nano Particles by Thermal Decomposition Method
Disclosed is a method of preparing pigmentary chromium oxide nano particles having 50 percent particle size less than about 100 nm. Preparation of nano chromium (III) oxide is investigated by thermal decomposition method. According to the disclosed method, a substantially dry solid composition of potassium dichromate and carbon active is heated in CO2 atmosphere to a temperature of about 60...
متن کاملLow-Temperature Selective Growth of Tungsten Oxide Nanowires by Controlled Nanoscale Stress Induction
We report a unique approach for the patterned growth of single-crystalline tungsten oxide (WOx) nanowires based on localized stress-induction. Ions implanted into the desired growth area of WOx thin films lead to a local increase in the compressive stress, leading to the growth of nanowire at lower temperatures (600 °C vs. 750-900 °C) than for equivalent non-implanted samples. Nanowires were su...
متن کاملGrowth of catalyst-free high-quality ZnO nanowires by thermal evaporation under air ambient
ZnO nanowires have been successfully fabricated on Si substrate by simple thermal evaporation of Zn powder under air ambient without any catalyst. Morphology and structure analyses indicated that ZnO nanowires had high purity and perfect crystallinity. The diameter of ZnO nanowires was 40 to 100 nm, and the length was about several tens of micrometers. The prepared ZnO nanowires exhibited a hex...
متن کاملAcetone Detection by Chemical Sensors Based on Tungsten and Titanium Oxide Nanowires
Tungsten and titanium oxide (WO3/Ti) nanowires (NWs) were grown by thermal oxidation of a tungsten and titanium alloy (WTi) metallic layer deposited on 2 × 2 mm2 alumina substrates by DC magnetron sputtering. Thermal oxidation was carried out in a custom evaporator chamber. Several parameters were controlled to achieve the optimal growth conditions. Morphological and structural analysis were pe...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Applied Physics Letters
سال: 2007
ISSN: 0003-6951,1077-3118
DOI: 10.1063/1.2734175