Synthesis of well-aligned ZnO nanorod arrays from mixed sulfide-oxide lead and zinc ore
نویسندگان
چکیده
منابع مشابه
Size-controlled growth of well-aligned ZnO nanorod arrays with two-step chemical bath deposition method
Well-aligned ZnO nanorod arrays (ZNAs) with different sizes in diameter were fabricated on Si substrates by two-step chemical bath deposition method (CBD), i.e. substrate pretreatment with spin coating to form ZnO nanoparticles layer and CBD growth. The effects of substrate pretreatments, pH, angel (θ) between substrate and beaker bottom and growth time (t) on the structure of ZNAs were investi...
متن کاملLow-temperature growth of well-aligned zinc oxide nanorod arrays on silicon substrate and their photocatalytic application
Well-aligned and single-crystalline zinc oxide (ZnO) nanorod arrays were grown on silicon (Si) substrate using a wet chemical route for the photodegradation of organic dyes. Structural analysis using X-ray diffraction, high-resolution transmission electron microscopy, and selected area electron diffraction confirmed the formation of ZnO nanorods grown preferentially oriented in the (001) direct...
متن کاملLeaching of Lead and Zinc from a Low-Grade Oxide Ore in Citric Acid Media
Leaching of a low-grade lead and zinc oxide ore was studied by an organic reagent, citric acid. The quadratic mathematical models were developed for the relationship among the influential parameters and lead and zinc recoveries. Leaching rate was strongly affected by the interactive effects of factors. It was also found that the quadratic effects of stirring speed and linear<e...
متن کاملWell-integrated ZnO nanorod arrays on conductive textiles by electrochemical synthesis and their physical properties
We reported well-integrated zinc oxide (ZnO) nanorod arrays (NRAs) on conductive textiles (CTs) and their structural and optical properties. The integrated ZnO NRAs were synthesized by cathodic electrochemical deposition on the ZnO seed layer-coated CT substrate in ultrasonic bath. The ZnO NRAs were regularly and densely grown as well as vertically aligned on the overall surface of CT substrate...
متن کاملSize-selected growth of transparent well-aligned ZnO nanowire arrays
This paper reports the effect of precursor concentration, growth temperature, and growth time on the size and density of ZnO nanowire arrays (ZNAs). The well-aligned ZNAs were grown on indium tin oxide substrate using a facile chemical bath deposition method. The results showed that the ZnO nanowires could be tailored to the desired sizes with a simple variation of the growth parameters. Optica...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Ceramics International
سال: 2016
ISSN: 0272-8842
DOI: 10.1016/j.ceramint.2016.08.181