Synthesis of Tungsten Heavy alloy Nanocomposite Powder by Ultrasonic-milling Process
نویسندگان
چکیده
منابع مشابه
SURFACE HARDENING OF TUNGSTEN-BASED HEAVY ALLOY VIA PACK BORONIZING
The boronizing of a tungsten heavy alloy containing Ni and Fe as the major alloying elements were performed in the present study to increase its surface hardening. Pack cementation method was employed as a well-known, successful solid-state process for boronizing. The coating treatment was accomplished at different temperatures of 1000, 1050 and 1100°C for 6 and 9 hours. The formation of tu...
متن کاملMechanical milling of aluminum powder using planetary ball milling process
Mechanical alloying has recently attracted considerable attention as researchers strive to enhance nanocomposite properties and extend their utility. The process can be performed at room temperature and homogeneous nanocomposite powders can be produced. In this paper, we investigated the effect of different ball milling parameters and operating conditions (milling time, ball size, processing co...
متن کاملMechanically Activated Combustion Synthesis of B4C-TiB2 Nanocomposite Powder
Boron carbide is one of the hardest materials. The combustion method was used to synthesize B4C-TiB2 nanocomposite powder in a B2O3-Mg-TiO2-C system. An experimental study of the formation of B4C–TiB2 nanoparticles was conducted in the thermal explosion mode. A mixture of B2O3:TiO2:Mg:C at a molecular ratio of 3:1:12:1 was chosen to obtain the B4C–TiB2. This powder mixture was milled for differ...
متن کاملDEVELOPMENT OF A TUNGSTEN HEAVY ALLOY, W-Ni-Mn, USED AS KINETIC ENERGY PENETRATOR
Abstract: The objective of this research was to develop a tungsten heavy alloy (WHA) having a microstructure and properties good enough to penetrate hard rolled steels as deep as possible. In addition this alloy should not have environmental problems as depleted uranium (DU) materials. For this purpose a wide spread literature survey was performed and on the base of information obtained in ...
متن کاملCryogenic Milling of Titanium Powder
Ti Grade 2 was prepared by cryogenic attritor milling in liquid nitrogen and liquid argon. Two types of milling balls were used—stainless steel balls and heavy tungsten carbide balls. The effect of processing parameters on particle size and morphology, contamination of powder and its microhardness was investigated. Milling in liquid nitrogen was not feasible due to excessive contamination by ni...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Korean Powder Metallurgy Institute
سال: 2007
ISSN: 1225-7591
DOI: 10.4150/kpmi.2007.14.2.101