Synthesis of tin nanorods via a sonochemical method combined with a polyol process
نویسندگان
چکیده
منابع مشابه
Sonochemical synthesis and characterization of NiMoO4 nanorods.
NiMoO(4) nanorods have been successfully synthesized by sonochemical method process by using Ni(CH(3)COO)(2) · 4H(2)O and (NH(4))(6)Mo(7)O(24) · 4H(2)O as starting materials. Some parameters including ultrasonic power, ultrasonic irradiation time, stirring effect, solvent effect, and surfactant effect were investigated to reach optimum condition. The as synthesized nanostructures were character...
متن کاملPolyol Process Synthesis of Monodispersed FePt Nanoparticles.
Monodispersed FePt nanoparticles are synthesized by reduction of iron(II) acetylacetonate and platinum(II) acetylacetonate with 1,2-hexadecanediol as the reducing reagent in the polyol process. As-prepared FePt nanoparticles are chemically disordered with fcc phase. Transmission electron microscopy (TEM) images show a self-assembled particle array with an average particle size of 3 nm and a sta...
متن کاملSynthesis of wide band gap nanocrystalline NiO powder via a sonochemical method.
A sonochemistry-based synthesis method was used to produce nanocrystalline nickel oxide powder with ≈ 20 nm average crystallite diameter from Ni(OH)(2) precursor. Ultrasound waves were applied to the primary solution to intensify the Ni(OH)(2) precipitation. Dried precipitates were calcined at 320°C to form nanocrystalline NiO particles. The morphology of the produced powder was characterized b...
متن کاملSynthesis and Characterization of CoAl2O4 Nano Pigments by Polyol Method
Blue nano pigments of CoAl2O4 were successfully prepared by polyol method. Two different groups of materials containing chloride and acetate compounds were used to synthesis the nano pigments. The nano pigments were calcinated at 1100 °C. The CoAl2O4 nano pigments were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), diffuse reflectance spectroscopy (DRS), dynamic li...
متن کاملSonochemical fabrication and characterization of stibnite nanorods.
Regular stibnite (Sb(2)S(3)) nanorods with diameters of 20-40 nm and lengths of 220-350 nm have been successfully synthesized by a sonochemical method under ambient air from an ethanolic solution containing antimony trichloride and thioacetamide. The as-prepared Sb(2)S(3) nanorods are characterized by employing techniques including X-ray powder diffraction, X-ray photoelectron spectroscopy, sca...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Ultrasonics Sonochemistry
سال: 2005
ISSN: 1350-4177
DOI: 10.1016/j.ultsonch.2004.02.001