SYNTHESIS OF STRUCTURALLY NOVEL CARBON MICRO/ NANOSPHERES BY LOW TEMPERATURE-HYDROTHERMAL PROCESS
نویسندگان
چکیده
منابع مشابه
Synthesis of Carbon Spheres of Controlled Size by Hydrothermal Method
Carbon Spheres were fabricated by hydrothermal method and their structural properties were investigated. Carbon Spheres with average sizes around of 230, 320 and 430 nm were synthesized in different concentration of glucose aqueous solution and different hydrothermal reaction time. The temperature of 180 °C by a hydrothermal reaction was fixed in all of glucose concentration and hydrothermal re...
متن کاملSynthesis and Characterization of Carbon Nanospheres Obtained by Hydrothermal Carbonization of Wood-derived and Other Saccharides
1: Department of Sustainable Bioproducts, Mississippi State University, Mississippi State, MS 39762-9820 2: Joint School of Nanoscience and Nanoengineering, North Carolina Agricultural and Technical State University, Greensboro, NC 27411 3: Dave C. Swalm School of Chemical Engineering, Mississippi State University, Mississippi State, MS 39762 4: Forest Products Lab, USDA Forest Service, Madison...
متن کاملLOW TEMPERATURE SYNTHESIS OF NANOCRYSTALLINE MgAl2O4 SPINEL VIA SUCROSE PROCESS
Abstract: Nanocrystalline MgAl2O4 spinel powder was synthesized using metal nitrates and a polymer matrix-based composed of sucrose and polyvinyl alcohol (PVA). The precursor and the calcined powders were characterized by simultaneous thermal analysis (STA), X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), and scanning electron microscopy (SEM). According to XRD res...
متن کاملInvestigation of hydrothermal process time on the size of carbon micro- and nano-spheres
In this study, carbon nano-micro spheres with tightly controllable size, regularand perfect shape, high yields and narrow size distribution were prepared simply fromglucose and DI water as precursors using a hydrothermal method. By setting the initialconcentration of glucose solution and changing the hydrothermal process time at aconstant temperature of 160 °C, carbon spheres with various sizes...
متن کاملLow temperature hydrothermal synthesis, characterization and optical properties of Sr6Nb10O30 – Nb2O5 nanocomposite
Sr6Nb10O30–Nb2O5 nanocomposite was synthesized in 2M NaOH aqueous solution. A stoichiometric 1:1 Sr:Nb molar ratio hydrothermal method at 120°C was used to synthesize this nanocomposite. Sr(NO3)2 and Nb2O5 were used as raw materials. The synthesized nanomaterials were characterized by powder X-ray diffraction (PXRD) technique. It was found that Sr6Nb10O30 was crystallized in tetragonal crystal ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Chilean Chemical Society
سال: 2013
ISSN: 0717-9707
DOI: 10.4067/s0717-97072013000300030