Synthesis of ordered mesoporous carbons with channel structure from an organic–organic nanocomposite
نویسندگان
چکیده
منابع مشابه
Synthesis of ordered mesoporous carbons with channel structure from an organic-organic nanocomposite.
Mesoporous carbons with ordered channel structure (COU-1) have been successfully fabricated via a direct carbonization of an organic-organic nanocomposite.
متن کاملSimple synthesis of Ni-containing ordered mesoporous carbons and their adsorption/desorption of methylene orange.
A simple route has been developed to synthesize magnetic Ni-containing ordered mesoporous carbons (Ni/OMCs) without using a solvent for dissolving carbon precursor or magnetic source. The adsorption and desorption of methylene orange (MO) on the obtained Ni/OMCs were investigated. The effects of Ni(NO(3))(2) loading amount and carbonization temperature on the morphologies, the structural parame...
متن کاملStructure Evolution of Ordered Mesoporous Carbons Induced by Water Content of Mixed Solvents Water/Ethanol
In this work, mesostructure evolution of ordered mesoporous carbons (OMCs) from the 2-D hexagonal (space group p6mm) to the discontinuous cubic [Formula: see text], then towards the face-centered cubic lattice [Formula: see text], and finally, to the simple cubic Pm3n is achieved by simply adjusting the cosolvent water content of the mixed solvents water/ethanol in the presence of a reverse non...
متن کاملTen Years of Research on Ordered Mesoporous Carbons: Major Advances in Synthesis, Properties and Potential Applications
About ten years ago Ryoo and co-workers [1,2] reported the hard-templating (HT) synthesis of ordered mesoporous carbons (OMCs) by using ordered mesoporous silicas (OMSs) as hard templates. Five years afterward the soft-templating (ST) synthesis of OMCs has been discovered [3-6]. Significant progress has been made in both hardand soft-templating synthesis of OMCs [7-10]. Major advances in the sy...
متن کاملControlled synthesis of highly dispersed platinum nanoparticles in ordered mesoporous carbons.
A novel route has been developed to fabricate ordered carbon mesoporous materials with well-dispersed, highly stable Pt nanoparticles of ca. 2-3 nm on the pore walls using platinum acetylacetonate as the co-feeding carbon and Pt precursor.
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Chem. Commun.
سال: 2005
ISSN: 1359-7345,1364-548X
DOI: 10.1039/b501259g