Synthesis of nickel and cobalt sulfide nanoparticles using a low cost sonochemical method
نویسندگان
چکیده
منابع مشابه
Synthesis of nickel and cobalt sulfide nanoparticles using a low cost sonochemical method
Nickel and cobalt sulfides are promising materials in different cutting-edge research areas like solar cells, supercapacitors, catalysts, and electrode materials. Nickel and cobalt sulfides with various stoichiometries have been synthesized sonochemically from Ni(CH3COO)2 ∙ 4H2O, Co(CH3COO)2 ∙ 2H2O and different sulfur precursors using a direct immersion ultrasonic probe. The products were char...
متن کاملsynthesis of amido alkylnaphthols using nano-magnetic particles and surfactants
we used dbsa and nano-magnetic for the synthesis of amido alkylnaphtols.
15 صفحه اولSonochemical Synthesis of Silver Nanoparticles Using Starch: A Comparison
A novel approach was applied to synthesize silver nanoparticles using starch under sonication. Colloidal silver nanoparticles solution exhibited an increase of absorption from 420 to 440 nm with increase starch quantity. Transmission electron microscopy followed by selected area electron diffraction pattern analysis indicated the formation of spherical, polydispersed, amorphous, silver nanopart...
متن کاملSonochemical Synthesis of Nickel Oxide Nano-particle
Nickel oxide (NiO) nanopowder was obtained during a sonochemical method. Nickel hydroxide precursor, prepared by addition of sodium hydroxide (NaOH) to nickel nitrate Ni(NO3)2 solution and vigorously stirring until the pH becomes 7.2. Ultrasounds waves were applied during precipitation period and after drying in oven nanopowder NiO was achieved. Transient and scanning electron microscopy showed...
متن کاملSynthesis and Surfactant Effect on Structural Analysis of Nickel Doped Cobalt Ferrite Nanoparticles by C-precipitation Method
Nanoparticles of nickel substituted cobalt ferrite (Nix Co1-xFe2 O4 : 0£ X£ 1) have been synthesized by co-precipitation method. Triton x-100 and oleic acid as surfactants were used. Particles size as estimated by the full width half maximum (FWHM) of the strongest X-ray diffraction (XRD) peak were found 17 and 21nm. Their morphology structure have been determined by scanning electron microscop...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Heliyon
سال: 2017
ISSN: 2405-8440
DOI: 10.1016/j.heliyon.2017.e00273