Synthesis of MgB2 from elements
Superconducting at 40 K MgB2 -samples were obtained by direct reaction from elements in molybdenum crucibles under argon pressure. Pressure allows to provide annealing at temperature up to 1400C, that resulting in rise of Tc and compactness of the ceramics, suggesting that there is a homogeneity range of composition for the compound.
متن کاملsynthesis of sulfides from alcohols and thiols in solvent-freeconditions and deoxygenation of sulfoxides
کاتالیست یک سنتز جدید برای تیواترها توصیف شده است. واکنش الکل ها با آریل، هتروآریل و آلکیل تیو ل ها درحضور 1،3،5- تری آزو- 2،4،6- تری فسفرین-2،2،4،4،6،6 هگزاکلراید ((tapc به عنوان یک کاتالیست موُثر، بازده های خوب تا عالی از تیواترها را حاصل می کند. علاوه براین، واکنش تحت شرایط بدون فلز و بدون حلال پیش می رود، بنابراین یک مکمل جالب برای روش های شناخته شده سنتز تیواترها ارائه می دهد. یک مکانیسم ا...
15 صفحه اولSuperconducting properties of MgB2 from first principles.
Solid MgB(2) has rather interesting and technologically important properties, such as a very high superconducting transition temperature. Focusing on this compound, we report the first nontrivial application of a novel density-functional-type theory for superconductors, recently proposed by the authors. Without invoking any adjustable parameters, we obtain the transition temperature, the gaps, ...
متن کاملSynthesis of MgB2 at Low Temperature and Autogenous Pressure
High quality, micron-sized interpenetrating grains of MgB₂, with high density, are produced at low temperatures (~420 °C < T < ~500 °C) under autogenous pressure by pre-mixing Mg powder and NaBH₄ and heating in an Inconel 601 alloy reactor for 5-15 h. Optimum production of MgB₂, with yields greater than 75%, occurs for autogenous pressure in the range 1.0 MPa to 2.0 MPa, with the reactor at ~50...
متن کاملIon beam synthesis of superconducting MgB2 thin films
Superconducting MgB2 thin films have been fabricated by 80 keV B ion implantation into commercial Mg ribbon with B doses up to 10 ions/cm, followed by thermal annealing at 500 °C. Temperature dependent dc magnetization measurements confirmed superconducting phase transitions between 11 and 18 K for samples containing nanocrystalline MgB2 grains embedded in Mg substrate with a small amount of Mg...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Physica C: Superconductivity
سال: 2001
ISSN: 0921-4534
DOI: 10.1016/s0921-4534(01)00917-0