Synthesis of Metastable Au-Fe Alloy Using Ordered Nanoporous Silica as a Hard Template
نویسندگان
چکیده
منابع مشابه
Synthesis of Metastable Au-Fe Alloy Using Ordered Nanoporous Silica as a Hard Template
Nanoporous Au-Fe alloy was synthesized via a wet chemistry route using ordered nanoporous silica as a hard template. The nanoporous Au-Fe consisted of aligned arrays of nanopores that were uniform in composition and ordered in hexagonal lattice, whereas Au-Fe nanoparticles synthesized without templates exhibited broad dispersions in the chemical composition and/or particle size. Nanoporous Au-F...
متن کاملOrdered Nanoporous Alumina Membranes Formed in Oxalic/Phosphoric Acid Using Hard Anodization
Highly self-ordered alumina nanopore arrays were fabricated using hard anodization technique in different mixtures of oxalic/phosphoric acid. The phosphoric acid concentration was varied from 0.05 to 0.3 M while the oxalic acid concentration was changed between 0.3 and 0.4 M. The self ordered nanoporous arrays were obtained in anodization voltage changing from 130 to 200 V. The interpore distan...
متن کاملFacile synthesis of highly ordered mesoporous silver using cubic mesoporous silica template with controlled surface hydrophobicityw
Recently, there has been great interest in the synthesis and application of various kinds of nanostructured noble metals such as platinum, gold and silver. Nanostructured silvers have been widely investigated as antimicrobial materials, bio-sensors, catalysts, and advanced materials exhibiting surface plasmon resonance and surface enhanced Raman scattering. All this research is mainly based on ...
متن کاملFacile synthesis of highly ordered mesoporous silver using cubic mesoporous silica template with controlled surface hydrophobicity.
Highly ordered mesoporous silver, which exhibits well-defined mesopores, high surface area and pore volume, has been successfully obtained using a cubic mesoporous silica, KIT-6, with controlled surface hydrophobicity as the hard template.
متن کاملSynthesis of uniform silica rods, curved silica wires, and silica bundles using filamentous fd virus as a template.
We explored fd as a template to direct the formation of silica nanomaterials with different morphologies through simple sol-gel chemistry[1]. Depending on the conditions silica nanowires can be formed, which seem to accurately transcript the bending conformation and the length of the fd viruses in solution. But also surprisingly straight silica rods may be formed, and under other conditions bow...