Synthesis of LaMgAl11O19 powders by reversed microemulsion method

Synthesis of Iron Yttrium Garnet Nanoparticles by Reverse Microemulsion Method

Colloidal nanodispersion of Iron Yttrium Garnet has been preparedbymixing the two ternary mixture of Triton X-100 (surfactant), n-heptane and aqueous solution that differing only in the aqueous phase.Ethanolwas added as cosurfactant and mixed them by ultrasound bath. By mixing these twomicroemulsions, Iron Yttrium garnet (Y3 Fe5 O12) nanodispersionwas obtained. Solids were settled by centrifuge...

SYNTHESIS OF AL2O3-NI COMPOSITE POWDERS BY CO-PRECIPITATION METHOD

The synthesis of micro-sized, uniformly distributed Al2O3-15Vol% Ni powders were studied through three step co-precipitation of hydroxides mixtures from proper solution, calcination at air atmosphere and final step of calcined powders in a carbon bed. Al and Ni hydroxide and amorphous phase were first obtained from their salt’s solutions through chemical co-precipitation method by adjusti...

Reverse Microemulsion Synthesis and Electrochemical Properties of LiNiO2 Powders

Lithium nickel oxide (LiNiO2) powders with an R3 m structure are successfully synthesized via a developed reverse microemulsion process. This method can effectively reduce the calcination temperature for synthesizing monophasic LiNiO2 powders to 700 C, which is much lower than that in the solid-state process. Nanosized LiNiO2 powders with narrow particle size distribution are obtained via the m...

Synthesis of Nanoparticles: Microemulsion Method

Synthesis of HfB2 Powders by Carbothermal Reduction

In this research, solid state carbothermal synthesis of HfB2 Nano powders was investigated. For this purpose, HfO2,H3BO3, carbon active or phenolic resin were used as raw materials for carbothermal reaction. After 2-4 hours of milling the raw materials by a planetary ball in an ethanol media, the mixture was heat dried and pressed in to disks under pressure of 20-30 bar. The disks were then pla...