Synthesis of hollow silica nanoparticles using poly (acrylic acid)-3,3’-diaminodipropylamine template
نویسندگان
چکیده
منابع مشابه
Synthesis of Hollow Silica Nanospheres with Microemulsion as Template
Materials: Cyclohexane, n-hexanol (98%), ammonia hydroxide (28~30 wt%), tetraethylorthosilicate (TEOS, 98%), (3-aminopropyl)trimethoxysilane (APTS, 95%), polyoxyethylene(10)isooctylphenylether (TritonX-100), fluorescein isothiocyanate isomer I (FITC, 90%), Iron(III) acetyl acetonate (Fe(acac)3, 99+%), and benzyl ether (99%) were purchased from Acrös. 1,2 dodecanediol (90%), oleylamine, and olei...
متن کاملSynthesis of pH Sensitive Hydrogels Based on Poly Vinyl Alcohol and Poly Acrylic Acid
In this research, hydrogels based on poly vinyl alcohol and poly acrylic acid blend were prepared which were cross-linked by applied thermal conditions. Afterward, effects of time and heating on water uptake were investigated. The highest water uptake value exhibited by the sample that was heated for 20 min. at 110 ºC was about 2129% after 4 days at equilibrium state. Hydrogels exhibited p...
متن کاملUniversal and facile synthesis of multicolored upconversion hollow nanospheres using novel poly(acrylic acid sodium salt) microspheres as templates.
A novel, fast and simple method was developed to fabricate poly(acrylic acid sodium salt) microspheres (PAAS MSs). The resulting PAAS MSs were utilized as active templates to universally synthesize the mesoporous lanthanide-doped gadolinium oxide hollow nanospheres with multicolored upconversion emissions under mild conditions.
متن کاملSynthesis, characterization and swelling behavior investigation of gelatin-g-Poly(Acrylic Acid-co-Itaconic Acid)
A novel pH-responsive superabsorbent hydrogel based on gelatin was prepared through crosslinking copolymerization of poly (acrylic acid) and poly (itaconic acid). The copolymerization conditions including monomers, initiator, gelatin and crosslinker concentration, reaction temperature, and neutralization percent were systematically optimized to achieve a hydrogel with swelling capacity as high ...
متن کاملSynthesis and Characterization of Poly (Acrylamide - co - Acrylic acid) Hydrogel Containing Silver Nanoparticles for Antimicrobial Applications
Acrylamide was copolymerized with acrylic acid at different ratios using potassium persulphate initiation system in presence of a crosslinking agent and different doses of silver nitrate to yield hydrogels containing silver nanoparticles upon post treatment with sodium hydroxide. Swelling capacity and kinetics of swelling of these hydrogels were studied. Size and distribution of the nanoparticl...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Colloids and Surfaces A: Physicochemical and Engineering Aspects
سال: 2015
ISSN: 0927-7757
DOI: 10.1016/j.colsurfa.2015.07.022