Synthesis of hexagonal structured wurtzite and chalcopyrite CuInS2 via a simple solution route
Wurtzite semiconductor CuInS2 [CIS] has been reported in recent years. As a kind of metastable structure, it is a great challenge to synthesize pure wurtzite CIS at low temperature. In this paper, via a simple and quick solution route, we synthesize both wurtzite- and chalcopyrite-structure CIS. Well-controlled wurtzite CIS hexagonal plates are obtained when an appropriate agent is added. The i...
متن کاملThe phase transformation of CuInS2 from chalcopyrite to wurtzite
In the present work, CuInS2 nanoparticles have been successfully synthesized by water-bath method with deionized water as solvent and thioglycolic acid as complexing agent at 80°C. The phase transition of CuInS2 from chalcopyrite to wurtzite was realized by adjusting the pH value of reaction solution. The emergence of Cu2S in the condition of higher pH value of reaction solution led to the form...
متن کاملPrecursor driven one pot synthesis of wurtzite and chalcopyrite CuFeS2.
A facile precursor dependent single step, one pot solution based synthesis of wurtzite and chalcopyrite polymorphs of CuFeS2 has been developed by reacting a Cu(I) thiourea complex with Fe2(SO4)3 and FeCl3 separately in ethylene glycol. The phases have been characterized by structural refinements, SEM-EDX, TEM-SAED, Raman, UV-Visible spectroscopy and TGA measurements.
متن کاملPreparation and characterization of Curcumin niosomal nanoparticles via a simple and eco-friendly route
In this investigation, curcumin niosomal nanoparticles were prepared via a simple, efficient and eco-friendly route, thin film hydration (TFH), in the presence of different mixture of the surfactants (tween 60 and span 60). Cholesterol ratio to surfactant, as effective factor, was altered to obtain the optimal nanoparticles. The size, zeta potential, size distribution, entrapment efficiency of ...
متن کاملSynthesis of dumbbell-like ZnO microcrystals via a simple solution route
Uniform dumbbell-like ZnO microcrystals had been successfully fabricated on a large scale via a facile solution technique under mild conditions. Obtained ZnO, with length of 1.2 to 1.6 μm and diameters of 350 to 600 nm, exhibited well-defined dumbbell-like morphology and hexagonal wurtzite structure and grew along the [001] direction. Effects of the reactant concentration on the sizes and morph...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Nanoscale Research Letters
سال: 2011
ISSN: 1556-276X
DOI: 10.1186/1556-276x-6-562