Synthesis of Functional Nano-Structured Powders Using Thermal Plasma Processing
نویسندگان
چکیده
منابع مشابه
Thermal Plasma Synthesis of Nano-sized Powders
Thermal plasmas, normally generated by DC (direct current) arc or inductively coupled RF (Radio Frequency) discharge, can be described as a high enthalpy flame with extremely high temperature fields (1,000~20,000 K) and a wide range of velocity fields from several m/s [1-5] to supersonic values [6-7]. Since the resultant huge enthalpy can be realized for various kinds of plasma forming gases an...
متن کاملsynthesis of amido alkylnaphthols using nano-magnetic particles and surfactants
we used dbsa and nano-magnetic for the synthesis of amido alkylnaphtols.
15 صفحه اولChemico- thermal synthesis of nano-structured cobalt with distinct magnetic property
The synthesis of nano- structured cobalt through a controlled chemical process followed by heat treating at various temperatures is studied. The product is characterized by ICP, XRD, FESEM , and TEM, indicating that the as- synthesized particles have an amorphous structure with 1.76 for Co/B ratio, an average size of 50 nm. The transformation of intermediate phases into single phase nano- cryst...
متن کاملSynthesis of Nano-Structured La0.6Sr0.4Co0.2Fe0.8O3 Perovskite by Co-Precipitation Method
Nano-structured lanthanum strontium cobalt ferrite, La0.6Sr0.4Co0.2Fe0.8O3 (LSCF), was successfully synthesized via co-precipitation method using metal nitrates as starting materials. Effects of precipitating agent and calcination temperature on the phase composition and morphology of synthesized powders were systematically studied using X-ray diffraction (XRD) and field emission scanning elect...
متن کاملSintering and Characterizations of WC-20wt.% (Fe,Co) Nano-Structured Powders Developed by Ball-Milling
The aim of the present work is to study the effects of the nanostructured WC-20 wt. % (Fe,Co) with different ratios of iron to cobalt on the microstructure and hardness of sintered samples. Furthermore, a sample with a cobalt binder under the same condition was produced for the comparison purposes. The nanocomposite development, after different milling times, has been monitored by means of X-ra...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Society of Powder and Powder Metallurgy
سال: 2007
ISSN: 0532-8799,1880-9014
DOI: 10.2497/jjspm.54.23