Synthesis of Flake Ag Powder by Polyol Process
نویسندگان
چکیده
منابع مشابه
Polyol Process Synthesis of Monodispersed FePt Nanoparticles.
Monodispersed FePt nanoparticles are synthesized by reduction of iron(II) acetylacetonate and platinum(II) acetylacetonate with 1,2-hexadecanediol as the reducing reagent in the polyol process. As-prepared FePt nanoparticles are chemically disordered with fcc phase. Transmission electron microscopy (TEM) images show a self-assembled particle array with an average particle size of 3 nm and a sta...
متن کاملSynthesis and Characterization of CoAl2O4 Nano Pigments by Polyol Method
Blue nano pigments of CoAl2O4 were successfully prepared by polyol method. Two different groups of materials containing chloride and acetate compounds were used to synthesis the nano pigments. The nano pigments were calcinated at 1100 °C. The CoAl2O4 nano pigments were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), diffuse reflectance spectroscopy (DRS), dynamic li...
متن کاملSYNTHESIS OF HIGH ASPECT RATIO SILVER NANOWIRES: PARAMETRIC STUDY OF THE POLYOL PROCESS
Silver nanowires (AgNWs) are considered as one-dimensional nanostructures, which have received much attention due to their nanoscale size, high aspect ratio, high electrical and thermal conductivity, optical transparency and high mechanical stability. Preparation of AgNWs by polyol process is remarkably sensitive to the interactions between synthesis parameters. In this study, the effect of the...
متن کاملSynthesis & Characterization of CaB4O7 Powder by Solid-State Reaction
The synthesis of calcium tetraborate was investigated in a temperature ranging from 800℃ to 900℃ using the solid-state reaction method. The synthesis was done using ammonium tetraborate tetrahydrate as the source of boron. At temperatures of 800 ℃ and 880 ℃, the mixed phases from different compounds were formed. At the optimum temperature of 840℃, the mixed phase was only composed of meta and t...
متن کاملDirect synthesis of partially ordered tetragonally structured FePt nanoparticles by polyol method for biomedical application
We report the direct soft chemical synthesis and characterization of a family of face centered cubic (fcc) and partially ordered face centered tetragonal (fct) FePt nanoparticles (NPs) suitable for biomedical applications. Both fcc and partially ordered fct-FePt NPs are synthesized by employing a simple polyol method. By using polyvinyl pyrolidone (PVP) as a stabilizer in various ratios during ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Korean Powder Metallurgy Institute
سال: 2004
ISSN: 1225-7591
DOI: 10.4150/kpmi.2004.11.6.477