Synthesis of boehmite powder from aluminum etching solution
نویسندگان
چکیده
منابع مشابه
synthesis of sulfides from alcohols and thiols in solvent-freeconditions and deoxygenation of sulfoxides
کاتالیست یک سنتز جدید برای تیواترها توصیف شده است. واکنش الکل ها با آریل، هتروآریل و آلکیل تیو ل ها درحضور 1،3،5- تری آزو- 2،4،6- تری فسفرین-2،2،4،4،6،6 هگزاکلراید ((tapc به عنوان یک کاتالیست موُثر، بازده های خوب تا عالی از تیواترها را حاصل می کند. علاوه براین، واکنش تحت شرایط بدون فلز و بدون حلال پیش می رود، بنابراین یک مکمل جالب برای روش های شناخته شده سنتز تیواترها ارائه می دهد. یک مکانیسم ا...
15 صفحه اولPreparation of nano gold powder from acid leaching tail solution
According to the unique properties and many applications of nano gold powder, it was prepared from an acid leaching tail solution. The low value residual gold ions existed in acid leaching tail solution in Mouteh gold mine in Iran with fellow heavy metals as pollutants (Fe2+, Cu2+, and Zn2+). Preparation of nano gold particles is achieved by two steps: First, by addition of ammonia as separatio...
متن کاملPreparation of nano gold powder from acid leaching tail solution
According to the unique properties and many applications of nano gold powder, it was prepared from an acid leaching tail solution. The low value residual gold ions existed in acid leaching tail solution in Mouteh gold mine in Iran with fellow heavy metals as pollutants (Fe2+, Cu2+, and Zn2+). Preparation of nano gold particles is achieved by two steps: First, by addition of ammonia as separatio...
متن کاملHydrothermal synthesis of microscale boehmite and gamma nanoleaves alumina
Novel uniform single-crystal boehmite leaf-like nanosheets with high anisotropy (with a lateral size of (4.5±0.5 μm)×(9.0±1.0 μm) and a thickness of 60–90 nm) and flower-like superstructures consisting of single-crystal petals were synthesized for the first time by a simple hydrothermal method. After calcination, those boehmite structures can be transformed into single-crystal gamma-alumina nan...
متن کاملMicrostructural Analysis of Boehmite Nanoparticles Prepared by Rapid Hydrolysis of Aluminum Sec-butoxide
Microstructural properties of six samples, prepared by rapid hydrolysis of aluminum secbutoxide, were investigated at RT using field emission scanning electron microscopy (FE SEM), X-ray powder diffraction (XRD) and Fourier transform infrared (FT-IR) spectrometry. The results of structural analysis show that, regardless of a significant difference in the processing parameters (pH, temperature, ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Korean Crystal Growth and Crystal Technology
سال: 2012
ISSN: 1225-1429
DOI: 10.6111/jkcgct.2012.22.6.286