Synthesis Mechanism of Nano BaTiO3 Particles at Low Temperature by Molten Salt Method
نویسندگان
چکیده
منابع مشابه
LOW TEMPERATURE MOLTEN SALT SYNTHESIS OF NANO CRYSTALLINE MgAl2O4 POWDER
Abstract: composition of MgO and nano boehmite. The reactant and potassium chloride, as the reaction media, were fired at800-1000 °C at different dwell times (0.5-5 h) in the ambient atmosphere. After washing and filtration, the spinel nanopowder was characterized by X-ray diffraction (XRD), Scanning electron microscopy (SEM), and Brunauer-Emmett-Teller (BET) techniques. It was demonstrated tha...
متن کاملLow temperature synthesis of CaZrO3 nanoceramics from CaCl2–NaCl molten eutectic salt
CaZrO3 nanoceramics were successfully synthesized at 700 C using the molten salt method, and the effects of processing parameters, such as temperature, holding time, and amount of salt on the crystallization of CaZrO3 were investigated. CaCl2, Na2CO3, and nano-ZrO2 were used as starting materials. On heating, CaCl2–NaCl molten eutectic salt provided a liquid medium for the reaction of CaCO3 an...
متن کاملsynthesis of amido alkylnaphthols using nano-magnetic particles and surfactants
we used dbsa and nano-magnetic for the synthesis of amido alkylnaphtols.
15 صفحه اولEFFECT OF ZrO2 PARTICLE SIZE ON MORPHOLOGY and SYNTHESIS OF NANO CaZrO3Via MOLTEN SALT METHOD
Well crystallized pure calcium zirconate (CaZrO3 ) nanopowder was successfully synthesized using the molten-salt method. CaCl2 , Na 2CO3, micro-ZrO 2and nano-ZrO 2 were used as starting materials. On heating, Na2CO3 reacted with CaCl 2to form NaCl and CaCO 3. Nano CaZrO 3 was formed by reacting equimolar amounts of in situformed CaCO 3 (or CaO) and ZrO 2 in molten Na 2CO3-NaCl e...
متن کاملSynthesis of Chromium Oxide Nano Particles by Thermal Decomposition Method
Disclosed is a method of preparing pigmentary chromium oxide nano particles having 50 percent particle size less than about 100 nm. Preparation of nano chromium (III) oxide is investigated by thermal decomposition method. According to the disclosed method, a substantially dry solid composition of potassium dichromate and carbon active is heated in CO2 atmosphere to a temperature of about 60...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Asian Journal of Chemistry
سال: 2014
ISSN: 0970-7077,0975-427X
DOI: 10.14233/ajchem.2014.17730