Synthesis, characterization and rheological behavior of pH sensitive poly(acrylamide-co-acrylic acid) hydrogels
نویسندگان
چکیده
منابع مشابه
Synthesis of pH Sensitive Hydrogels Based on Poly Vinyl Alcohol and Poly Acrylic Acid
In this research, hydrogels based on poly vinyl alcohol and poly acrylic acid blend were prepared which were cross-linked by applied thermal conditions. Afterward, effects of time and heating on water uptake were investigated. The highest water uptake value exhibited by the sample that was heated for 20 min. at 110 ºC was about 2129% after 4 days at equilibrium state. Hydrogels exhibited p...
متن کاملStructural Parameters and Swelling Behavior of pH Sensitive Poly(acrylamide-co-acrylic acid) Hydrogels
In the present work, hydrogels based on acrylamide (AAm) and acrylic acid (AAc), crosslinked with N,N’-methylenebisacrylamide (MBAAm) were prepared by free radical polymerization in solution. The effect of initial AAm/AAc mole ratio and nominal crosslinking ratio (moles of crosslinking agent/moles of polymer repeat unit) on the dynamic and equilibrium swelling behaviour of hydrogels was investi...
متن کاملSynthesis, characterization and swelling behavior investigation of gelatin-g-Poly(Acrylic Acid-co-Itaconic Acid)
A novel pH-responsive superabsorbent hydrogel based on gelatin was prepared through crosslinking copolymerization of poly (acrylic acid) and poly (itaconic acid). The copolymerization conditions including monomers, initiator, gelatin and crosslinker concentration, reaction temperature, and neutralization percent were systematically optimized to achieve a hydrogel with swelling capacity as high ...
متن کاملsynthesis of ph sensitive hydrogels based on poly vinyl alcohol and poly acrylic acid
in this research, hydrogels based on poly vinyl alcohol and poly acrylic acid blend were prepared which were cross-linked by applied thermal conditions. afterward, effects of time and heating on water uptake were investigated. the highest water uptake value exhibited by the sample that was heated for 20 min. at 110 ºc was about 2129% after 4 days at equilibrium state. hydrogels exhibited ph-sen...
متن کاملPreparation and characterization of pH sensitive crosslinked Linseed polysaccharides-co-acrylic acid/methacrylic acid hydrogels for controlled delivery of ketoprofen
Some pH responsive polymeric matrix of Linseed (Linum usitatissimum), L. hydrogel (LSH) was prepared by free radical polymerization using potassium persulfate (KPS) as an initiator, N,N-methylene bisacrylamide (MBA) as a crosslinker, acrylic acid (AA) and methacrylic acid (MAA) as monomers; while ketoprofen was used as a model drug. Different formulations of LSH-co-AA and LSH-co-MAA were formul...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Arabian Journal of Chemistry
سال: 2017
ISSN: 1878-5352
DOI: 10.1016/j.arabjc.2013.11.027