Synthesis and Thermal Stability of Melamine-Formaldehyde-Nitro Aniline Ion-Exchange Resin
نویسندگان
چکیده
منابع مشابه
Synthesis and Thermal Degradation Studies of Melamine Formaldehyde Resins
Melamine formaldehyde (MF) resins have been synthesized at different reaction temperature and pH values. Different molar ratios of melamine and formaldehyde were used to synthesize the corresponding resins. The prepared resin samples were characterized by using molecular weight determination viscometry and thermogravimetric analysis (TGA). The maximum percentage of solid content (69.7%) was obt...
متن کاملThermal Degradation and Stability of Accelerated-curing Phenol-formaldehyde Resin
In order to study the thermal stability of accelerated-curing PF resin, the curing behavior of fresh PF resin was investigated in the presence of single accelerator of methylolurea derivatives (MMU), magnesium hydrate (Mg(OH)2), 25% aqueous solution of sodium carbonate (Na2CO3), and propylene carbonate (PC). Also their optimum combination was added in fresh PF resin. The thermal stability of cu...
متن کاملSynthesis and application of formaldehyde free melamine glutaraldehyde amino resin as an effective retanning agent
Novel melamine based free formaldehyde resin using glutaraldehyde as a condensing agent rather than formaldehyde has been synthesized under optimum conditions for use as a retanning agent. Characteristics and effects of the polymer as a retanning agent have been investigated against conventional melamine formaldehyde resin. Tear strength, tensile strength, elongation at break, and scanning elec...
متن کاملThe Effects of Adding Melamine at Different Resin Synthesis Points of Low Mole Ratio Urea-Melamine- Formaldehyde (UMF) Resins
Low mole ratio urea-melamine-formaldehyde (UMF) resins synthesized with 2.5% and 5.0% melamine levels added at the beginning, middle, and end points of the first alkaline step of the typical urea-formaldehyde (UF) resin synthesis procedure were compared with typical UMF resins synthesized with melamine additions made at the final alkaline step. Various resin analysis, particleboard preparation,...
متن کاملRattan Cane Modified with Polyethylene Glycol Melamine-Urea-Formaldehyde Resin
To effectively improve the strength of Plectocomia pierreana rattan cane without reducing its toughness, the cane was impregnated with a new water-soluble melamine-urea-formaldehyde (MUF) resin modified with low-molecular-weight polyethylene glycol (PEG), marked as PMUF. The PMUF synthetic process was optimized using an orthogonal test L9(3). Results showed that the dimensional stability, densi...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: International Letters of Chemistry, Physics and Astronomy
سال: 2014
ISSN: 2299-3843
DOI: 10.18052/www.scipress.com/ilcpa.32.112