Synthesis and sintering properties of composite nano-Ag–Sn slurry
نویسندگان
چکیده
This topic prepared a composite nano-silver–tin slurry. According to the boiling point of dispersant, 300 °C is determined as sintering temperature. As amount tin added increases, shear strength Ag–Sn slurry gradually increases. When 1/20, reaches maximum 50 MPa. The increase in due strengthening second phase. exceeds drops sharply, mainly overgrowth Ag3Sn, product reaction silver and tin. porosity was measured accurately by Photoshop software. porosities pure silver, 5% tin, 10% samples are 21.8%, 16.8%, 12.5%, respectively. Brinell hardness with 20.60N/mm2 97.79N/mm2, After adding small nano-tin, its increased density, decreases, value Compared nano-silver slurry, performance improved. Therefore, it provides certain reference for preparation
منابع مشابه
synthesis of amido alkylnaphthols using nano-magnetic particles and surfactants
we used dbsa and nano-magnetic for the synthesis of amido alkylnaphtols.
15 صفحه اولSintering properties of zirconia-based ceramic composite
This study examines the effects of different ZrB2 content on various mechanical properties and electrical conductivity of ZrB2/Y-TZP composite. Composites with ZrB2 content of up to 20 wt-% were particularly beneficial at the lower sintering temperature range by achieving greater densification and better hardness than Y-TZP monolith. In contrast to the trends estimated from rule of mixture, the...
متن کاملextraction and characterization of allium irancum plant extract and its application in the green synthesis of silver nano particles and oxidation of thiocarbony1 compounds
سنتز سبز نانوذرات فلزی (nps) درسالهای اخیر توجه بسیارزیادی را به خود جلب کرده است. زیرا این پروتوکل کم هزینه وسازگار با محیط زیست از روش های استاندارد سنتز. در این پایان نامه ما گزارش میکنیم یک روش ساده و سازگار با محیط زیست برای سنتز نانوذرات نقره با استفاده از محلول آبی عصاره گیاه allium iranicum به عنوان یک عامل کاهش دهنده ی طبیعی. نانو ذرات نقره مشخص شد با استفاده از تکنیک های uv-visible، x...
nano-rods zno as an efficient catalyst for the synthesis of chromene phosphonates, direct amidation and formylation of amines
چکیده ندارد.
some properties of fuzzy hilbert spaces and norm of operators
in this thesis, at first we investigate the bounded inverse theorem on fuzzy normed linear spaces and study the set of all compact operators on these spaces. then we introduce the notions of fuzzy boundedness and investigate a new norm operators and the relationship between continuity and boundedness. and, we show that the space of all fuzzy bounded operators is complete. finally, we define...
15 صفحه اولذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: AIP Advances
سال: 2023
ISSN: ['2158-3226']
DOI: https://doi.org/10.1063/5.0139775