Synthesis and characterizations of nickel doped Co-Zn-Y ferrites

Interfacial Dielectric Losses in Co-Doped Ni-Zn Ferrites

The temperature and fresuency dependence of tg8 and E' for Nk ~Ztb ferrites was studied in the 10'lo6 Hz frequency range and 20-200°C temperrhrre tange. The experimental curves exhibit aspects very dependent of composition. To verify Ulat interfacial losses, expected to appear in this type of system are compatible with the experimental results a calculation of the dielectric permittivity and di...

Synthesis and Thermoelectric Behavior in Nanoparticles of Doped Co Ferrites

Samples of CoFe2-xCrxO4 where x varies from 0.0 to 0.5 were prepared by co-precipitation route. These samples were sintered at 750°C for 2 hours. These particles were characterized by X-ray diffraction (XRD) at room temperature. The FCC spinel structure was confirmed by XRD patterns of the samples. The crystallite sizes of these particles were calculated from the most intense peak by Scherrer f...

Elastic behaviour of Sn doped Ni-Zn ferrites

The polycrystalline Sn added Ni-Zn ferrites were prepared using the conventional sintering method. The monophasic nature of the samples was characterized using X-rays. The elastic behavior has been measured in the temperature range 80-410oC using the composite oscillator method. The values of Young’s and shear modulus are corrected to theoretical density using the method of Mackenzie method. Th...

Enhancement of the Magnetic Properties for Co-Mn-Zn Ferrites

Aluminum substituted cobalt manganese zinc ferrite nanoparticles Co0.425Mn0.425Zn0.150AlxFe2-xO4 (from x= 0.0 to 0.15 with step 0.025) have been synthesized by chemical co-precipitation route. X-ray diffraction (XRD) and infrared spectroscopy (FTIR) revealed that the obtained powders have a single phase of cubic spinel structure. The crystallite sizes calculated from XRD data have been confirme...

Plasma Synthesis of Facetted Nickel nano-Ferrites with Controlled Stoichiometry