Synthesis and Adsorption Property of SiO2@Co(OH)2 Core-Shell Nanoparticles
Silica nanoparticles were directly coated with cobalt hydroxide by homogeneous precipitation of slowly decomposing urea in cobalt nitrate solution. The cobalt hydroxide was amorphous, and its morphology was nanoflower-like. The BET (Brunauer-Emmett-Teller) surface area of the core-shell composite was 221 m²/g. Moreover, the possible formation procedure is proposed: the electropositive cobalt io...
متن کاملSynthesis and characterization of monodisperse silica-polyaniline core-shell nanoparticles.
Monodisperse silica-polyaniline core-shell nanoparticles with an average diameter of 26 nm were synthesized by in-situ polymerisation of aniline monomers adsorbed on the silica surface through electrostatic interactions.
متن کاملSynthesis and Characterization of Core-shell ZrO2/PAAEM/PS Nanoparticles
This work demonstrates the synthesis of core-shell ZrO2/PAAEM/PS nanoparticles through a combination of sol-gel method and emulsifier-free emulsion polymerizaiton. By this method, the modified nanometer ZrO2cores were prepared by chemical modification at a molecular level of zirconium propoxide with monomer of acetoacetoxyethylmethacrylate (AAEM), and then copolymerized with vinyl monomer to fo...
متن کاملSynthesis and Properties of Magnetic-Optical Core-Shell Nanoparticles.
Due to their high integrity, facile surface chemistry, excellent stability, and dual properties from the core and shell materials, magnetic-plasmonic core-shell nanoparticles are of great interest across a number of science, engineering and biomedical disciplines. They are promising for applications in a broad range of areas including catalysis, energy conversion, biological separation, medical...
متن کاملSynthesis and Luminescence Properties of Core/Shell ZnS:Mn/ZnO Nanoparticles
In this paper the influence of ZnO shell thickness on the luminescence properties of Mn-doped ZnS nanoparticles is studied. Transmission electron microscopy (TEM) images showed that the average diameter of ZnS:Mn nanoparticles is around 14 nm. The formation of ZnO shells on the surface of ZnS:Mn nanoparticles was confirmed by X-ray diffraction (XRD) patterns, high-resolution TEM (HRTEM) images,...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Nanomaterials
سال: 2015
ISSN: 2079-4991
DOI: 10.3390/nano5020554