Sustainable glasses in the SiO2–P2O5–CaO–K2O system from waste and concentrated solar power

Sustainable glasses were prepared by green technology including the use of different wastes as raw materials and concentrated solar power (CSP) renewable energy. The used to formulate animal bone flour ash, which presents high contents CaO, P2O5 alkaline oxides; glassy sand from waste packaging glass submitted a primary treatment, composed principally SiO2; potassium carbonate reagent grade. Different exposure times radiation tested. For comparison, same composition was melted into conventional electric furnace. CSP produce reduces melting time approximately 90%, with consequent energy savings. increased processing results in more amorphous thermally stable glasses. showed viability producing ecofriendly SiO2–P2O5–CaO–K2O system, could be matrix-based fertilizers. Se prepararon vidrios sostenibles mediante una tecnología alternativa que incluye el uso de diferentes residuos como materias primas y energía concentrada (ESC) fuente renovable. Las utilizadas para formular los fueron ceniza harina hueso animal, presenta altos contenidos óxidos alcalinos; arena vítrea procedente envases vidrio sometidos un tratamiento primario, compuesta principalmente por SiO2, carbonato potásico grado reactivo. evaluó efecto del tiempo exposición la radiación sobre las características obtenidos. Como material referencia se empleó misma composición obtenido en horno eléctrico convencional. El ESC producir reduce fusión aproximadamente con consiguiente ahorro energía. aumento procesamiento da lugar más amorfos mayor estabilidad térmica. Los resultados mostraron viabilidad producción sistema SiO2-P2O5-CaO-K2O, podrían utilizarse fertilizantes.