Surface strengthening and grain refinement of AZ31B magnesium alloy by ultrasonic cavitation modification
نویسندگان
چکیده
منابع مشابه
Grain Refinement and Enhancement of Mechanical Properties of Hot Extruded Rare-Earth Containing Magnesium Alloy
The effects of rare earth addition and hot extrusion process on the grain refinement of magnesium alloy were studied. The as-cast Mg-6Al-1Zn (AZ61) alloy had the average grain size of ~ 64 µm and its microstructure consisted of α-Mg and Mg17Al12 phase. By partial substitution of Al with Gd to reach Mg-4.8Gd-1.2Al-1Zn alloy, it was observed that the Mg17Al12 phase disappeared and two new interme...
متن کاملProcess Mechanics and Surface Integrity Induced by Dry and Cryogenic Machining of AZ31B-O Magnesium Alloy
The corrosion resistance of magnesium alloys depends mainly on its surface integrity. Previous experimental studies have shown that machining can induces small (nano-scale) grain size, compressive residual stresses and basal plane crystallographic texture, which significantly improve the corrosion resistance of magnesium alloy. These studies have focused on the positive effects of cryogenic coo...
متن کاملConstitutive Modelling of AZ31B-O Magnesium Alloy for Cryogenic Machining
The success of a FE model for metal cutting process is strongly dependent on the accurate characterization of the workpiece material, under similar conditions as those found in metal cutting. In this paper, dynamic shear tests using a Gleeble machine have been performed on 4 mm thickness disks of AZ31B-O magnesium alloy, using a special designed tool. In order to include the effects of the cryo...
متن کاملWire Arc Additive Manufacturing of AZ31 Magnesium Alloy: Grain Refinement by Adjusting Pulse Frequency
Wire arc additive manufacturing (WAAM) offers a potential approach to fabricate large-scale magnesium alloy components with low cost and high efficiency, although this topic is yet to be reported in literature. In this study, WAAM is preliminarily applied to fabricate AZ31 magnesium. Fully dense AZ31 magnesium alloy components are successfully obtained. Meanwhile, to refine grains and obtain go...
متن کاملEFFECT OF GRAIN REFINEMENT AND MODIFICATION OF EUTECTIC PHASE ON SHRINKAGE OF AlSi9Cu3 ALLOY
All metals and alloys with exception of Bi are shrinking during cooling, mostly during the solidification process. In order to avoid shrinking porosity, casting process, and gating and feeding system must be properly designed. Solidification front must move towards the feeding system where solidification is then completed. No separate liquid pockets where solidification ended without feeding sh...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Chinese Journal of Aeronautics
سال: 2021
ISSN: 1000-9361
DOI: 10.1016/j.cja.2020.08.043