Surface Nanocrystallization of 35# Type Carbon Steel Induced by Ultrasonic Impact Treatment (UIT)
نویسندگان
چکیده
منابع مشابه
Introductory fatigue tests on welded joints in high strength steel and aluminium improved by various methods including ultrasonic impact treatment (UIT)
This paper summarizes fatigue test on high strength steel specimens in the as-welded condition and specimens treated by ultrasonic impact treatment, TIG dressing and a combination of TIG dressing and ultrasonic impact treatment. Single lap joint specimens in 6 mm aluminium plate material were tested in the as-welded, hammer peened, needle peened and ground condition. Aluminium joints with longi...
متن کاملNANOCRYSTALLIZATION MECHANISMS OF Fe52Cr18Mo7B16C4Nb3 BULK AMORPHOUS STEEL
Crystallization kinetics of Fe52Cr18Mo7B16C4Nb3 alloy was evaluated using X-ray diffraction, differential scanning calorimetric (DSC) tests and TEM observations in this research work. In effect, crystallization and growth mechanisms were investigated using DSC tests in four different heating rates (10, 20, 30, 40 K/min) and kinetic models (i.e. Kissinger- Starink, Ozawa, and Matusita methods). ...
متن کاملEnhancing Fatigue Strength by Ultrasonic Impact Treatment
Enhancement in fatigue performance of welded joints by Ultrasonic Impact Treatment (UIT) was evaluated in large-scale specimens having a nominal yield strength of 345 to 690 MPa. Eighteen rolled-beam specimens having welded details at cover plates and transverse stiffeners and eight built-up specimens having only transverse stiffener details were fatigue tested after treating them by UIT. A par...
متن کاملEffects of Ultrasonic Treatment during the Solidification Process on the Structure Formation of Low Carbon Steel
This paper studied effects of ultrasonic treatment during the solidification process on structure formation of low carbon steel. Results showed that with ultrasonic treatment grains were refined and the steel ingot avoided the cast widmanstatten structure. When ultrasonic treatment was employed, pearlite was broken and the average length of pearlite was decreased from 550mm to 140mm. The corres...
متن کاملSurface Nanocrystallization of Stainless Steel with ZAF Method and SEM Technique
From a nano electronic circuit designer’s point of view the growth of ultrathin film in the ultra high vacuum chamber (UHVC) would imply better stainless steel structure. ZAF method and SEM (scanning Electron Microscopy) technique are used to realize surface nano crystallizafion on an stailness steel sample. The as-welded condition of UHVC is also studied to see if this chamber can prevent weld...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Procedia Engineering
سال: 2012
ISSN: 1877-7058
DOI: 10.1016/j.proeng.2011.12.641