Surface Characterization of Three-Layer Organic Coating Applied on AISI 4130 Steel
نویسندگان
چکیده
منابع مشابه
Tribological Properties of B4C-Ni Cermet Coating Produced by HVOF Process on the Surface of 4130 Steel
In this research, B4C-Ni cermet coating was sprayed on the surface of 4130 steel from B4C and Ni feed-stockpowders using high velocity oxy-fuel (HVOF) method. In order to characterize the tribological behavior of thecoating, ball on disk wear tests were done at the ambient temperature and under the loads of 1, 3 and 5 N.Phase analysis of the coating after spraying was studied ...
متن کاملDuplex Surface Treatment of AISI 1045 Steel via Plasma Nitriding of Titanized Layer
In this Study, surface of medium carbon steel (AISI 1045) was modified by titanizing followed by plasma nitriding. Titanizing was performed using pack cementation method, in a pack mixture of ferrotitanium, ammonium chloride and alumina, at 1223 K for 45 and 180 min. Plasma-nitriding was conducted at two temperatures of 803 and 823 K for 5 h, in a gas mixture of 75%N2+25%H2. The samples were c...
متن کاملtribological properties of b4c-ni cermet coating produced by hvof process on the surface of 4130 steel
in this research, b4c-ni cermet coating was sprayed on the surface of 4130 steel from b4c and ni feed-stockpowders using high velocity oxy-fuel (hvof) method. in order to characterize the tribological behavior of thecoating, ball on disk wear tests were done at the ambient temperature and under the loads of 1, 3 and 5 n.phase analysis of the coating after spraying was studied by x-ray diffracto...
متن کاملDevelopment of Copper-Ferrite Spinel Coating on AISI 430 Steel Used as Solid Oxide Fuel Cell
The bare and pre-oxidized AISI 430 pieces were screen printed by copper ferrite spinel coatings. Good bonding between the coating and the substrate was achieved by the reactive sintering process of the reduced coating. The energy dispersive X-ray spectroscopy (EDS) analysis revealed that the scale is a double layer consisting of a chromia-rich subscale and an outer Cu/Fe-rich spinel. The result...
متن کاملSTUDY ON NIOBIUM CARBIDE COATING FORMATION ON AISI L2 STEEL USING THERMO-REACTIVE DEPOSITION METHOD
In the present research, to form niobium carbide coating on the surface of AISI L2 steel Thermo-Reactive Deposition method (TRD) in a molten bath was used. Niobium carbide coating treatment was carried out at 1173 K, 1273 K, and 1373 K for 2, 4, and 8 hours. The molten bath contained 20wt.% borax (Na2B4O7), 5 wt.% boric acid (B2O3), and 75 wt.% ferro-niobium. The presence and properties of...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Advances in Materials Science and Engineering
سال: 2018
ISSN: 1687-8434,1687-8442
DOI: 10.1155/2018/6767245