Surface and subsurface rolling contact fatigue characteristic depths and proposal of stress indexes

Analysis of Surface Crack Growth under Rolling Contact Fatigue

Understanding the fatigue crack growth phenomenon in railheads requires a study of driving forces such as the crack tip opening and sliding displacements, under repeated rolling contact. Finite element simulations, allowing elastic-plastic deformation, and mixed-mode crack growth laws were utilized to demonstrate that the fatigue crack growth rates display a minimum after a finite amount of cra...

Rolling contact fatigue of surface coatings—a review

The aim of this review is to survey the state of the art relating to the rolling contact fatigue (RCF) investigation of various overlay coatings and also, to ascertain the influence of design parameters such as the type of deposition process, coating material and thickness on the RCF performance. Rolling contact fatigue is a significant factor in the failure of components in rolling/sliding con...

Rolling contact fatigue in martensitic 100Cr6: subsurface hardening and crack formation

Rolling contact fatigue tests on 100Cr6 steel were carried out with a ballon-rod tester. Microstructural damage was manifested by gradual hardness changes under the subsurface, and microcracks formed adjacent to inclusions; both being evidence of plastic deformation. The hardness increase appears to be due to the development of residual stress, while the microcracks form as a result of the conc...

Rolling Contact Fatigue in Ultra High Vacuum

the study of bright and surface discrete cavity solitons dynamics in saturable nonlinear media

امروزه سالیتون ها بعنوان امواج جایگزیده ای که تحت شرایط خاص بدون تغییر شکل در محیط منتشر می-شوند، زمینه مطالعات گسترده ای در حوزه اپتیک غیرخطی هستند. در این راستا توجه به پدیده پراش گسسته، که بعنوان عامل پهن شدگی باریکه نوری در آرایه ای از موجبرهای جفت شده، ظاهر می گردد، ضروری است، زیرا سالیتون های گسسته از خنثی شدن پراش گسسته در این سیستم ها بوسیله عوامل غیرخطی بوجود می آیند. گسستگی سیستم عامل...