Suppression of the magnetocrystalline bulk anisotropy in thin epitaxial Co(110) films on Cu(110)
نویسندگان
چکیده
منابع مشابه
Reorientation of magnetic anisotropy in epitaxial cobalt ferrite thin films
A. Lisfi,1,* C. M. Williams,1 L. T. Nguyen,2 J. C. Lodder,2 A. Coleman,1 H. Corcoran,1 A. Johnson,1 P. Chang,1 A. Kumar,1 and W. Morgan1 1Department of Physics, Morgan State University, 1700 E. Cold Spring Lane, Baltimore, Maryland 21251, USA 2SMI, MESA Institute for Nanotechnology, University of Twente, P.O. Box 217, 7500 AE Enschede, The Netherlands Received 27 March 2007; revised manuscript ...
متن کاملStacking Faults and Their Effect on Magnetocrystalline Anisotropy in Co and Co-Alloy Thin Films
Stacking faults in (1010) unicrystal Co and Co-alloy thin films have been analyzed by the electron diffraction technique. As predicted no diffraction contrast of stacking faults could be observed when the beam is parallel to the [1010] direction. However, both by plan-view TEM observation and electron diffraction along the [1120] direction reveal that the stacking fault density in biased pure C...
متن کاملProbing magnetic anisotropy effects in epitaxial CrO2 thin films
The magnetic anisotropy in ferromagnetic chromium dioxide thin films (Tc;393 K) grown epitaxially on ~100! TiO2 substrates, is probed using precise rf transverse susceptibility (xT) measurements. Singular peaks in xT are observed that are associated with the anisotropy (6HK) and switching (6Hs) fields in CrO2. Theoretical calculations of xT based on a simple coherent rotation model display rema...
متن کاملEffects of substrate bias on magnetocrystalline anisotropy Ku of CoPt thin films with increasing Pt content
The magnetocrystalline anisotropy Ku of continuous Co1−xPtx alloy films peaks at 30 at. % of Pt. Further increase in Pt at. % decreases Ku quickly probably due to the increasing density of stacking faults SFs and the fcc phases. The effect of substrate bias has been studied in various compositions of CoPt films. Ku increases from 8 10 6 to 1.1 107 ergs /cm3 when 50 V bias was applied to Co60Pt4...
متن کاملMicroscopic origin of the reduced magnetocrystalline anisotropy with increasing oxide content in Co80Pt20:oxide thin films
Angle-dependent x-ray magnetic circular dichroism at the Co L2.3 edges has been utilized to systematically study Co80Pt20 : WO3 perpendicular magnetic recording thin films, in which the magnetocrystalline anisotropy significantly drops as the oxide volume fraction increases. The microscopic origin of this phenomenon in the studied films can be mainly attributed to an increase in orbital moment ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Physical Review B
سال: 1996
ISSN: 0163-1829,1095-3795
DOI: 10.1103/physrevb.53.r10548