Superplasticity in Fine (NiAl+Ni<SUB>3</SUB>Al) Two Phase Alloy
نویسندگان
چکیده
منابع مشابه
Enhanced superplasticity in commercially pure titanium alloy
The superplasticity of commercially pure titanium alloy at high temperature was studied and the dynamic recrystallization phenomenon of the alloy was investigated by using electron back scattered diffraction. A two-step deformation method was used to increase the ductility of the alloy from 188% to 243%. 2004 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
متن کاملSuperplasticity of a fine-grained Mg–1.5 wt% Gd alloy after severe plastic deformation
The strain rate sensitivity (SRS) of Mg–1.5 wt% Gd processed by conventional extrusion and 2 passes of simple shear extrusion (SSE) was investigated by shear punch testing. Shear punch tests were conducted at initial shear strain rates in the range of 0.003–0.3 s-1 and at temperatures in the range of 573–773 K. A fine-grained microstructure with an average grain size of about 2.5 µm, obtained a...
متن کاملsynthesis of platinum nanostructures in two phase system
چکیده پلاتین، فلزی نجیب، پایدار و گران قیمت با خاصیت کاتالیزوری زیاد است که کاربرد های صنعتی فراوانی دارد. کمپلکس های پلاتین(ii) به عنوان دارو های ضد سرطان شناخته شدند و در شیمی درمانی بیماران سرطانی کاربرد دارند. خاصیت کاتالیزوری و عملکرد گزینشی پلاتین مستقیماً به اندازه و- شکل ماده ی پلاتینی بستگی دارد. بعضی از نانو ذرات فلزی در سطح مشترک مایع- مایع سنتز شده اند، اما نانو ساختار های پلاتین ب...
Achieving superplasticity in a Bi-Sn alloy processed by equal- channel angular pressing
Equal-channel angular pressing (ECAP) was utilized to process a Bi‒42Sn eutectic alloy at room temperature using processing route A for 1, 2, 4, and 8 passes. Tensile testing was performed at room temperature under initial strain rates in the range of 1.0 × 10 -5 to 1.0 × 10 -2 s -1 . The results demonstrate that processing by ECAP improves the ductility in this material and the elongations to ...
متن کاملFine Structure in Multi-Phase Zr8Ni21-Zr7Ni10-Zr2Ni7 Alloy Revealed by Transmission Electron Microscope
The microstructure of an annealed alloy with a Zr₈Ni21 composition was studied by both scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The presence of three phases, Zr₈Ni21, Zr₂Ni₇, and Zr₇Ni10, was confirmed by SEM/X-ray energy dispersive spectroscopy compositional mapping and TEM electron diffraction. Distribution of the phases and their morphology can be linked...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Institute of Metals and Materials
سال: 1989
ISSN: 0021-4876,1880-6880
DOI: 10.2320/jinstmet1952.53.2_249