Supercritical Drying for Nanostructure Fabrication.
نویسندگان
چکیده
منابع مشابه
Laser Focusing of Atoms for Nanostructure Fabrication
Laser-focusing of atoms has emerged as a viable form of nanofabrication. Structures are formed by focusing chromium atoms as they deposit onto a surface. The focusing occurs in a standing-wave laser field in one or two dimensions, resulting in arrays spaced at exactly half the laser wavelength ( /2 = 212.78 nm). Atomic force, scanning electron, and transmission electron microscopies are used to...
متن کاملNickel electroplating for nanostructure mold fabrication.
We demonstrated a practical process of fabricating nickel molds for nanoimprinting. Dual-side polished glass is chosen as the substrate on which nickel nanostructures are successfully electroplated. Photonic crystal structures with 242 nm diameters and other nanoscale pillars down to 9 nm diameters are achieved over a large area. The electroplating parameters are investigated and optimized. Thi...
متن کاملFabrication of activated carbon fibers/carbon aerogels composites by gelation and supercritical drying in isopropanol
Activated carbon fiber/carbon aerogel (ACF/CA) composites were fabricated by gelling a mixture of ACF and resorcinol and furfural, followed by supercritical drying of the mixture in isopropanol. The product then went through carbonization in a nitrogen atmosphere. The fabrication conditions, such as the mass content of R–F, the content of the ACF added, and the gelation temperature, were explor...
متن کاملSupercritical Gel Drying of Polymeric Hydrogels for Tissue Engineering Applications
Tissue engineering (TE) is an emerging field aimed at repairing defective tissues and organ, instead of relying on conventional organ transplantation. Among the polymeric materials proposed for TE applications, the water-soluble polymers have been frequently used in form of hydrogels, that are a class of highly hydrated polymer materials. Nevertheless, hydrogel materials have poor mechanical pr...
متن کاملFabrication and nanostructure of oriented FePt particles
Thin films of oriented tetragonal FePt particles separated by amorphous alumina have been fabricated by electron beam evaporation. The ordering of the FePt particles without coarsening can be tailored by annealing conditions. The value of coercivity of the annealed film reached as high as 4.4 kOe. The perpendicular magnetic coercivity of the annealed film was slightly larger than in-plane coerc...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Photopolymer Science and Technology
سال: 2002
ISSN: 0914-9244,1349-6336
DOI: 10.2494/photopolymer.15.381