Sulphide Corrosion Cracking of High Strength Steel
نویسندگان
چکیده
منابع مشابه
Corrosion at Sulphide Inclusions in Stainless Steel
Auger analysis was performed using a high resolution scanning auger electron microscope and auger electron spectroscopy. Elemental auger contour maps for corroded sulphide inclusions in stainless steel were presented. It was found that the copper enriched-manganese sulphide inclusions were uniformly corroded, which might be due to CU2S deposition on the surface of corroding inclusions. In contr...
متن کاملHydrogen-assisted stress corrosion cracking of high strength steel Division of Surface and Corrosion Science School of Chemical Science and Engineering Royal Institute of Technology, KTH
In this work, Slow Strain Rate Test (SSRT) testing, Light Optical Microscopy (LOM) and Scanning Electron Microscopy (SEM) were used to study the effect of microstructure, corrosive environments and cathodic polarisation on stress corrosion cracking (SCC) of two grades of high strength steels, Type A and Type B. Type A is manufactured by quench and tempered (Q&T) method. Type B, a normalize stee...
متن کاملStress- Corrosion Crack Initiation of High-strength Pipeline Steel in Near-neutral pH Environments
Stress-corrosion cracking (SCC) tests were conducted in the near-neutral pH standard solution, NS4, and in an actual soil solution, using four-point bending at a high stress ratio and low frequency conditions very similar to those of operational pipelines. Pitting incubation appeared first and then pitting initiated and grew in both solutions although there were many more pits on the specimen t...
متن کاملCORROSION BEHAVIOR OF ZINC COATED STEEL REBAR IN HIGH-STRENGTH REINFORCED CONCRETE
A large number of reinforced concrete structures subjected to chloride ions. Two basicapproaches for preventing corrosion of reinforcing steel embedded in concrete are: Increasing theconsolidation of concrete and using different coating on rebars. In present research steel rebarsare coated in different ways: a) 40 µm of zinc electroplated on steel rebar b) Zinc powder withepoxy paste (zinc rich...
متن کاملA Comparison of Hydrogen Embrittlement and Stress Corrosion Cracking in High Strength Steels
The purpose of this study was to compare the known behavior of hydrogen embrittled high-strength steel to the characteristics of environmentallyinduced stress corrosion failure where hydrogen is continuously generated at the specimen surface. The incubation time for the initiation of slow crack growth was accelerated by prestressing for a fixed time below the lower critical limit. These results...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Tetsu-to-Hagane
سال: 1968
ISSN: 0021-1575,1883-2954
DOI: 10.2355/tetsutohagane1955.54.5_610