SUBSTITUSI FILLER DENGAN LIMBAH KARBIT TERHADAP CAMPURAN ASPAL PANAS HOT ROLLED SHEET – BASE COURSE (HRS-BC)

In hot asphalt mixtures, fillers are used, used as between coarser aggregate particles, also function to increase the binding energy (cohesion) of concrete. This study uses waste carbide an alternative filler in HRS-BC mixture, this aims determine results Marshall test, namely stability, VFWA, VMA, VIM, Flow, and MQ. research experimental method. Composition Variation The substitution is 0%, 40%, 50%, 60% weight filler. obtained a mixture 0% with stability values 871.13 kg, VFWA 75.18 VMA 22.55 VIM 7.01 flow 3.80 mm, MQ 229.29. variation 40% value 629.20 65.69 25.09 10.05 2.85 226.52. 50% 1011.76 72.75 23.15 7.72 2.50 410.00. 1291.26 71.67 23.41 8.04 2.30 562.35. from it can be concluded that use at most effective according General Specifications Division 6: 2016 Asphalt Pavement.ABSTRAKDalam campuran aspal panas digunakan bahan pengisi filler,Filler sebagai antar partikel agregat yang lebih kasar,filler juga berfungsi meningkatkan energi ikat (kohesi) pada beton. penelitian ini menggunakan limbah karbit alternatif pengganti HRS-BC, bertujuan untuk mengetahui hasil pengujian marshall test yaitu stabilitas,VFWA,VMA,VIM,Flow,dan Penelitian metode Eksperimen. Komposisi Variasi Substitusi sebesar dan dari berat didapatkan variasi nilai stabilitas 871,13 75,18 22,55 7,01 3,80 229,29. 629,20 65,69 25,09 10,05 2,85 226,52. 1011,76 72,75 23,15 7,72 2,50 410,00. 1291,26 71,67 23,41 8,04 2,30 562,35. dapat disimpulkan bahwa penggunaan adalah paling efektif sesuai Spesifikasi Umum Divisi 6 : Perkerasan Aspal.