Study on Hot-Working Behavior of High Carbon Steel / Low Carbon Steel Composite Material Using Processing Map
نویسندگان
چکیده
منابع مشابه
Static Strain Aging Behavior of Low Carbon Steel Drawn Wire
The static strain aging is a phenomenon that can change the mechanical properties of low carbon steels. Thus, the static strain aging behavior of low carbon steel wires after drawing process is studied. To do so, the wires are austenitized at different temperatures and cooled in different rates. Then the wires are drawn and aged at a specific temperature and time. Before and after aging of each...
متن کاملRecrystallization Behavior of Deep Drawing Low Carbon Steel Sheets Produced by Mobarakeh Steel Plant
In the present work the recrystallization behavior of deep drawing grade Al-killed low carbon steel sheets produced by Mobarakeh Steel Plant (MSP) has been studied. Salt bath isothermal annealing has b...
متن کاملFailure Investigation of Hydrogen Blistering on Low-strength Carbon Steel
The current study assesses the root causes of hydrogen blisters on low strength carbon steel equipment. For this purpose, some experiments including hardness test, non-destructive test (NDT), metallography, and fractograpghy are conducted. The microstructure of two blisters is assessed by means of optical microscopy and scanning electron microscopy (SEM). The microstructural studies show that t...
متن کاملOptimization of Hot Workability in Ti-IF Steel by Using the Processing Map
Processing map for hot working of Ti-IF steel has been developed in the temperature range of 750 to 1100 °C and strain rate of 0.01 to 100 s-1. This map in the austenite region exhibits a single domain with a peak efficiency of 45% occurring at 1025 °C and strain rate of 0.02 s-1. The domain extends over the temperature range of 1000 to 1100 °C and strain rate range of 0.01 to 1 s-1. The true s...
متن کاملEFFECT OF HIGH TEMPERATURE OXIDATION ON THE CORROSION BEHAVIOR OF ALUMINIZED LOW CARBON STEEL IN MOLTEN ALUMINUM
Hot dip aluminizing was carried out on the low carbon steel rod under optimized conditions. The aluminized samples were further oxidized at 1000̊C in air atmosphere at two different times of 20 and 60 minutes. Microstructure study and phase analysis were studied by scanning electron microscopy and X-ray diffraction methods, respectively. The characterization of the coating showed that, Fe2...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Key Engineering Materials
سال: 2014
ISSN: 1662-9795
DOI: 10.4028/www.scientific.net/kem.622-623.330