Study on heat treatment to improve the microstructure and corrosion behavior of ZK60 magnesium alloy
نویسندگان
چکیده
منابع مشابه
Effect of Deformation-Induced Defects on the Microstructure and Pitting Corrosion Behavior of Al-Ag Alloy
In this study, a wide range of combined ageing treatments and cold work deformations in the Al 4.2 wt% Ag alloy matrix were proposed, aiming to investigate the effect of defects such as precipitates (Ag2Al plates) and dislocations on the mechanical and electrochemical behavior of Al–4.2 wt% Ag alloys. Further reductions of thickness from 10 to 60%, decreases the mean size of Ag2...
متن کاملEffect of heat treatment on corrosion and electrochemical behaviour of AZ91D magnesium alloy
An AZ91D ingot in the as-cast condition was homogenized by solution treatment and then aged for various periods of time. The microstructures produced were studied in detail and the b phase volume fraction was measured quantitatively. The Corrosion resistance of all the different microstructures was studied in 3.5% NaCl solution through weight loss measurement in constant immersion conditions an...
متن کاملCorrosion Behavior of the Friction Stir Welded AZ31 Magnesium Alloy.
* IDMEC, Instituto Superior Técnico, Universidade de Lisboa, Av. Rovisco Pais, 1049-001 Lisboa, Portugal ** DEQ/ICEMS, Instituto Superior Técnico, Universidade de Lisboa, Av. Rovisco Pais, 1049001 Lisboa, Portugal. *** Department of Engineering Design and Production, School of Engineering, Aalto University, P.O. Box 1420, FI-00076 Aalto, Finland **** Faculdade de Engenharia da universidade do P...
متن کاملEFFECTS OF Al-5TI-1B MASTER ALLOY AND HEAT TREATMENT ON THE MICROSTRUCTURE AND DRY SLIDING WEAR BEHAVIOR OF AN Al-12Zn-3Mg-2.5Cu ALLOY
In this study the effect of Al–5Ti–1B grain refiner on the structural characteristics and wear properties of Al–12Zn–3Mg–2.5Cu alloy was investigated. The optimum amount for Ti containing grain refiners was selected as 2 wt.%. T6 heat treatment, (i.e. heating at 460 °C for 1 h before water quenching to room temperature and then aging at 120 °C for 24 h) was applied for all specimens before wear...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Materials Research and Technology
سال: 2020
ISSN: 2238-7854
DOI: 10.1016/j.jmrt.2020.08.004