Study on Corrosion Behavior of as-forged AZ81 Mg alloy in different concentrations of NaCl solution
نویسندگان
چکیده
منابع مشابه
Effect of solution treatment on stress corrosion cracking behavior of an as-forged Mg-Zn-Y-Zr alloy
Effect of solid solution treatment (T4) on stress corrosion cracking (SCC) behavior of an as-forged Mg-6.7%Zn-1.3%Y-0.6%Zr (in wt.%) alloy has been investigated using slow strain rate tensile (SSRT) testing in 3.5 wt.% NaCl solution. The results demonstrated that the SCC susceptibility index (ISCC) of as-forged samples was 0.95 and its elongation-to-failure (εf) was only 1.1%. After T4 treatmen...
متن کاملEffect of solution treatment on the fatigue behavior of an as-forged Mg-Zn-Y-Zr alloy
Through investigating and comparing the fatigue behavior of an as-forged Mg-6.7Zn-1.3Y-0.6Zr (wt.%) alloy before and after solid solution treatment (T4) in laboratory air, the effect of T4 treatment on fatigue crack initiation was disclosed. S-N curves illustrated that the fatigue strength of as-forged samples was 110 MPa, whereas the fatigue strength of T4 samples was only 80 MPa. Observations...
متن کاملCorrosion Behavior of Novel Mg-9Li-7Al-1Sn and Mg-9Li-5Al-3Sn-1Zn Alloys in NaCl Aqueous Solution
Corrosion behavior of two multiphase Mg-Li-Al-based alloys in 0.6 M NaCl aqueous solution is investigated by hydrogen gas evolution measurement and electrochemical test. This paper reports, for the first time, the comparison of hydrogen evolution and Tafel extrapolation results of Mg-Li-Al-based alloys. The corrosion rate of Mg-9Li-7Al-1Sn is observed to be reasonably higher when compared to th...
متن کاملElectrochemical Behavior of Nanocrystalline Fe88Si12 Alloy in 3.5% NaCl Solution
Influence of microstructure on electrochemical behavior of nanocrystalline Fe88Si12 alloy has been investigated in 3.5 wt% NaCl solution. The results show that Fe88Si12 alloy with optimal corrosion resistance is composite of ordered Fe3Si and disordered Fe(Si) phases and grain size of 40 nm. Because the ordered Fe3Si structure is beneficial to form SiO2 film, which possesses good corrosion resi...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Physics: Conference Series
سال: 2021
ISSN: 1742-6588,1742-6596
DOI: 10.1088/1742-6596/1750/1/012084