Study of the synthesis of MAX phase Ti3SiC2 powders by pressureless sintering

MAX phases exhibit excellent combination of ceramic and metallic-like properties. In this work, phase Ti3SiC2 powder was synthesized starting-off with different combinations elemental powders carbides. The used were Ti, Si, C, SiC TiC in combinations, molar ratios size. Powders heat treated on a vacuum furnace for times temperatures situ production the phase. High purity samples analyzed by X-ray diffraction (XRD) scanning electron microscopy (SEM) order to identify quantify constituents present. main produced TiSi2. Up 94% obtained using Ti:SiC:C as starting ratio 3:1.5:0.5. Different constitution observed surface centre samples. An optimal composition, ratio, treatment temperature time is proposed formation high Selected mixture studied thermodynamically reaction mechanism proposed. Las fases presentan una excelente combinación de propiedades cerámicas y metálicas. En este trabajo se sintetizaron polvos fase partir diferentes combinaciones elementales carburos. Los utilizados fueron en combinaciones, proporciones molares tamaño partícula. sinterizaron un horno vacío tiempos temperaturas para la producción Ti3SiC2. muestras sintetizadas alta pureza analizaron mediante difracción rayos X microscopía electrónica barrido identificar cuantificar las constituyentes presentes. principales los producidos Se obtuvo hasta utilizando como partida proporción 3:1,5:0,5. observó diferente formación superficie el centro muestras. Finalmente, propone composición óptima polvo partida, relación molar, temperatura sinterización tiempo pureza. La mezcla seleccionada estudió termodinámicamente mecanismo reacción MAX.