Study of NiCu multilayer magnetic nanowires
نویسندگان
چکیده
منابع مشابه
CoFe Layers Thickness and Annealing Effect on the Magnetic Behavior of the CoFe/Cu Multilayer Nanowires
CoFe/Cu multilayer nanowires were electrodeposited into anodic aluminum oxide templates prepared by a two-step mild anodization method, using the single-bath technique. Nanowires with 30 nm diameter and the definite lengths were obtained. The effect of CoFe layers thickness and annealing on the magnetic behavior of the multilayer nanowires was investigated. The layers thickness was controlled t...
متن کاملElectrochemical fabrication of Cu/Pd multilayer nanowires in polycarbonate template
In this work,copper/palladium (Cu/Pd) multilayer nanowires were successfully prepared by electrodeposition method using polycarbonate template. The fabrication of Pd/Cu multilayer nanowires was controlled by analyzing the current–time transient during electrodeposition using potentiostat. The morphological properties of the nanowires were studied by scanning electron microscopy (SEM) and resu...
متن کاملMagnetic Properties of Ni0.3Fe0.7 Alloy Nanowires
The effect of length variation on the magnetic properties of NiFe alloy nanowires electrodeposited into the alumina template was investigated. The diameter (45±2.5 nm) and length (~ 1.9, 7.12, 8.3, 9.5 and 13.3 µm) of the nanowires were estimated from scanning electron microscopy images. Energy dispersive spectroscopy results showed Ni3Fe7 composition of the alloy nanowire...
متن کاملcofe layers thickness and annealing effect on the magnetic behavior of the cofe/cu multilayer nanowires
cofe/cu multilayer nanowires were electrodeposited into anodic aluminum oxide templates prepared by a two-step mild anodization method, using the single-bath technique. nanowires with 30 nm diameter and the definite lengths were obtained. the effect of cofe layers thickness and annealing on the magnetic behavior of the multilayer nanowires was investigated. the layers thickness was controlled t...
متن کاملInvestigations of Microstructures and Magnetic Properties through Off-time between Pulses and Controlled Cu Content in Pulse Electrodeposited NiCu Nanowires
NiCu alloy nanowires arrays were embedded into the anodic aluminum oxide (AAO) template by ac-pulse electrodeposition. Different off-time were used in electrolyte with constant concentration of Ni and Cu and acidity of 3. The effect of deposition parameters on alloy contents was investigated by studying the microstructure and magnetic properties of as-deposited NiCu alloy nanowires. Atomic forc...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Revista dos Trabalhos de Iniciação Científica da UNICAMP
سال: 2018
ISSN: 2596-1969
DOI: 10.20396/revpibic262018217