Study of Microstructure and Modification Effect of Mg-Sr Master Alloy on AZ91D Magnesium Alloy

Microstructure and Aging Behavior of Nonflammable AZ91D Mg Alloy

Phase equilibria of AZ91D Mg alloys for nonflammable use, containing Ca and Y, were carried out by using FactSage® and FTLite database, which revealed that solid solution treatment could be performed at temperatures from 400 to 450C. Solid solution treatment of AZ91D Mg alloy without Ca and Y was successfully conducted at 420C and supersaturated microstructure with all beta phase resolved into ...

Microstructure and corrosion characteristics of laser-alloyed magnesium alloy AZ91D with Al-Si powder.

Blown-powder laser surface alloying was performed on the magnesium alloy AZ91D with Al-Si alloy powder to improve corrosion resistance. Characterization by scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and x-ray diffraction (XRD) analysis revealed that intermetallic compounds (IMCs) of Mg2Si, Al12Mg17 and Al3Mg2 were formed in the matrix of α-Mg and Al solid solutions...

Tensile and fatigue behavior of AZ91D magnesium alloy

Recently magnesium alloys, owing to their low density and excellent specific strength have been attractive to designers as an advanced material for coping with energy conservation and environmental pollution regulations. Much of the recent developments of magnesium alloys and processes have been driven by the requirements of the aerospace industry, although some successful ones have found appli...

Effect of heat treatment on corrosion and electrochemical behaviour of AZ91D magnesium alloy

An AZ91D ingot in the as-cast condition was homogenized by solution treatment and then aged for various periods of time. The microstructures produced were studied in detail and the b phase volume fraction was measured quantitatively. The Corrosion resistance of all the different microstructures was studied in 3.5% NaCl solution through weight loss measurement in constant immersion conditions an...

Microstructure-sensitive investigation of magnesium alloy fatigue