Investigation on Mechanical and Electrical Properties of Cu-Ti Nanocomposite Produced by Mechanical Alloying
In this paper, Cu-Ti nanocomposite synthesized via ball milling of copper-titanium powders in 1, 3, and 6 of weight percentage compounds. The vial speed was 350 rpm and ball to powder weight ratio kept at 15:1 under Argon atmosphere, and the time of milling was 90 h. Obtained powders were studied by scanning electron microscopy (SEM), X-ray diffraction (XRD), and dynamic light scattering (DLS)....
متن کاملHydrogen evolution activity of NiMo-MoO2 produced by mechanical milling
In this study, mechanical alloying was done by a high-energy planetary ball milling technique. A mixture of NiO and MoO3 and graphite powders were used as initial materials. After milling of powder mixture with 40 wt.% additional graphite, a temperature of 400, 550 and 1000 °C for 1 h was considered for the heat treatment of powder mixture. Also, powder mixtures containing 60, 80 and 100 wt.% a...
متن کاملRaney-nickel Catalysts Produced by Mechanical Alloying
Raney catalysts were prepared by a combination of mechanical alloying and leaching as an alternative in the synthesis of Raney-Nickel catalysts. Binary Al-Ni and ternary Al-Ni-Fe alloys with nominal compositions Al65Ni35, Al75Ni25, Al65Ni30Fe5, Al75Ni20Fe5 (in atomic percent), were processed from pure elemental powders; they consisted mainly of the intermetallic B2 AlNi phase. Aluminum was sele...
متن کاملProduction of Fe-TiN and Fe-Ti(N,C) composite powders by mechanical alloying
In this research, the production of Fe-TiN and Fe-Ti(N,C) composite powders by mechanical alloying was investigated and evaluated. Ferrotitanium (containing 70%Ti), titanium and graphite were used as the raw materials. Initial mixtures were milled in different time durations under the pure nitrogen atmosphere with the pressure of 5atm. The results showed that when N2 pressure is 5 at...
متن کاملAging of a nanostructured Zn50Se50 alloy produced by mechanical alloying
The aging of a nanocrystalline equiatomic ZnSe alloy produced by mechanical alloying was investigated using X-ray diffraction (XRD) and differential scanning calorimetry (DSC) techniques. The measured XRD patterns showed that Se atoms located at interfacial component migrated with aging giving raise to a crystalline selenium (c-Se) phase. DSC spectra of heat-treated samples at temperatures abov...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Materials for Renewable and Sustainable Energy
سال: 2013
ISSN: 2194-1459,2194-1467
DOI: 10.1007/s40243-013-0009-y